Rutile-type Mn F2 was shock loaded at pressures of 3.6-33.4 GPa by the impact of flyer plates accelerated by a propellant gun. Recovered samples were examined by x-ray powder diffraction analysis and transmission electron microscopy (TEM). A phase transition from the rutile-type structure to the α-Pb O2 -type structure was found above 3.6 GPa. The yield of the α-Pb O2 phase in the recovered samples increased for pressures of up to about 10 GPa and decreased at higher pressures. This phenomenon can be explained by a residual temperature effect. A lamellar pattern consisting of two crystalline phases (rutile and α-Pb O2 -type Mn F2) was observed in the shocked sample by TEM observation. The shock-induced phase transition from the rutile-type structure to the α-Pb O2 -type structure was inferred to proceed via fluorite-related structures or a Pb Cl2 -type structure by comparison with results of previous static high-pressure experiments.
|Journal||Physical Review B - Condensed Matter and Materials Physics|
|Publication status||Published - Sep 28 2007|
All Science Journal Classification (ASJC) codes
- Electronic, Optical and Magnetic Materials
- Condensed Matter Physics