### Abstract

Raising a transition temperature (formula presented) in organic radical ferromagnets is a desire for material scientists. We investigated the pressure effects on an organic radical ferromagnet 2,5-difluorophenyl-α-nitronyl nitroxide (2,5-DFPNN), which has a ferromagnetic transition at 0.45 K. The hydrostatic pressure effects were investigated through measurements of ac magnetic susceptibility (χ) up to (formula presented) heat capacity (formula presented) up to (formula presented) and powder x-ray diffraction up to (formula presented) Furthermore, ac magnetic susceptibility under nonhydrostatic pressure was also measured in the pressure region up to 10.0 GPa. As for 2,5-DFPNN, we observed the pressure-induced enhancement of (formula presented) as (formula presented) (formula presented) while other prototypes, the β phase of p-NPNN and (formula presented) show the negative pressure effects. The results for the (formula presented) and the crystal structural analysis suggest that the magnetic dimension of the short-range order developing above (formula presented) transforms from one dimension (a axis) to two dimensions (ac plane) under high pressure. This increase of the magnetic dimension probably promotes to increase (formula presented) The ferromagnetic signal of χ, however, decreases with increasing pressure, and finally disappears for (formula presented) The decrease seems to originate from the decrease of the ferromagnetic interaction along the b axis. Similar instability of organic ferromagnetic long range order against pressure has been observed for the β phase of p-NPNN and (formula presented)

Original language | English |
---|---|

Journal | Physical Review B - Condensed Matter and Materials Physics |

Volume | 67 |

Issue number | 2 |

DOIs | |

Publication status | Published - Jan 1 2003 |

### Fingerprint

### All Science Journal Classification (ASJC) codes

- Electronic, Optical and Magnetic Materials
- Condensed Matter Physics

### Cite this

*Physical Review B - Condensed Matter and Materials Physics*,

*67*(2). https://doi.org/10.1103/PhysRevB.67.024427

**Pressure effects on an organic radical ferromagnet : 2,5-difluorophenyl-α-nitronyl nitroxide.** / Mito, M.; Deguchi, H.; Tanimoto, T.; Kawae, T.; Nakatsuji, S.; Morimoto, H.; Anzai, H.; Nakao, H.; Murakami, Y.; Takeda, K.

Research output: Contribution to journal › Article

*Physical Review B - Condensed Matter and Materials Physics*, vol. 67, no. 2. https://doi.org/10.1103/PhysRevB.67.024427

}

TY - JOUR

T1 - Pressure effects on an organic radical ferromagnet

T2 - 2,5-difluorophenyl-α-nitronyl nitroxide

AU - Mito, M.

AU - Deguchi, H.

AU - Tanimoto, T.

AU - Kawae, T.

AU - Nakatsuji, S.

AU - Morimoto, H.

AU - Anzai, H.

AU - Nakao, H.

AU - Murakami, Y.

AU - Takeda, K.

PY - 2003/1/1

Y1 - 2003/1/1

N2 - Raising a transition temperature (formula presented) in organic radical ferromagnets is a desire for material scientists. We investigated the pressure effects on an organic radical ferromagnet 2,5-difluorophenyl-α-nitronyl nitroxide (2,5-DFPNN), which has a ferromagnetic transition at 0.45 K. The hydrostatic pressure effects were investigated through measurements of ac magnetic susceptibility (χ) up to (formula presented) heat capacity (formula presented) up to (formula presented) and powder x-ray diffraction up to (formula presented) Furthermore, ac magnetic susceptibility under nonhydrostatic pressure was also measured in the pressure region up to 10.0 GPa. As for 2,5-DFPNN, we observed the pressure-induced enhancement of (formula presented) as (formula presented) (formula presented) while other prototypes, the β phase of p-NPNN and (formula presented) show the negative pressure effects. The results for the (formula presented) and the crystal structural analysis suggest that the magnetic dimension of the short-range order developing above (formula presented) transforms from one dimension (a axis) to two dimensions (ac plane) under high pressure. This increase of the magnetic dimension probably promotes to increase (formula presented) The ferromagnetic signal of χ, however, decreases with increasing pressure, and finally disappears for (formula presented) The decrease seems to originate from the decrease of the ferromagnetic interaction along the b axis. Similar instability of organic ferromagnetic long range order against pressure has been observed for the β phase of p-NPNN and (formula presented)

AB - Raising a transition temperature (formula presented) in organic radical ferromagnets is a desire for material scientists. We investigated the pressure effects on an organic radical ferromagnet 2,5-difluorophenyl-α-nitronyl nitroxide (2,5-DFPNN), which has a ferromagnetic transition at 0.45 K. The hydrostatic pressure effects were investigated through measurements of ac magnetic susceptibility (χ) up to (formula presented) heat capacity (formula presented) up to (formula presented) and powder x-ray diffraction up to (formula presented) Furthermore, ac magnetic susceptibility under nonhydrostatic pressure was also measured in the pressure region up to 10.0 GPa. As for 2,5-DFPNN, we observed the pressure-induced enhancement of (formula presented) as (formula presented) (formula presented) while other prototypes, the β phase of p-NPNN and (formula presented) show the negative pressure effects. The results for the (formula presented) and the crystal structural analysis suggest that the magnetic dimension of the short-range order developing above (formula presented) transforms from one dimension (a axis) to two dimensions (ac plane) under high pressure. This increase of the magnetic dimension probably promotes to increase (formula presented) The ferromagnetic signal of χ, however, decreases with increasing pressure, and finally disappears for (formula presented) The decrease seems to originate from the decrease of the ferromagnetic interaction along the b axis. Similar instability of organic ferromagnetic long range order against pressure has been observed for the β phase of p-NPNN and (formula presented)

UR - http://www.scopus.com/inward/record.url?scp=0037222754&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0037222754&partnerID=8YFLogxK

U2 - 10.1103/PhysRevB.67.024427

DO - 10.1103/PhysRevB.67.024427

M3 - Article

AN - SCOPUS:0037222754

VL - 67

JO - Physical Review B - Condensed Matter and Materials Physics

JF - Physical Review B - Condensed Matter and Materials Physics

SN - 1098-0121

IS - 2

ER -