Strain localization in copper canister FSW welds for spent nuclear fuel disposal

A. Forsström, S. Bossuyt, Y. Yagodzinskyy, K. Tsuzaki, H. Hänninen

Research output: Contribution to journalArticle

Abstract

Spent nuclear fuel disposal in copper canisters in a deep geologic repository is planned in Finland and Sweden. The purpose of the copper shell is to perform as a ductile corrosion barrier to prevent radioactive substances from leaking into the environment. Therefore, the most important property of the copper shell, besides the good corrosion resistance, is its ductility. The copper canisters are sealed by friction stir welding (FSW), which results in strong welds when compared to the base materials, but the microstructural heterogeneity introduced by the welding may also lead to strain localization. Thus, the strain localization behavior of two different copper canister welds was studied by tensile tests in combination with digital image correlation (DIC). The main difference between the welds is the utilization of shielding gas to reduce oxidation during welding. The shielding gas improves the stability of the welding process, as well as reduces the number of oxide particles in the welds. It is known, that oxide particles are detrimental in copper in the presence of hydrogen. Therefore, the two welds were also thermally hydrogen charged to study hydrogen trapping in the weld material. Thermal desorption measurements (TDS) show that considerable hydrogen uptake occurs in the weld oxide zone, but it did not compromise the ductility of the copper welds in these tests. However, the DIC tests indicate considerably earlier strain localization on the retreating side of the new weld, welded with the shielding gas. This is attributed to differences in the initial state of the lid materials.

Original languageEnglish
Pages (from-to)347-359
Number of pages13
JournalJournal of Nuclear Materials
Volume523
DOIs
Publication statusPublished - Sep 2019

Fingerprint

cans
friction stir welding
spent fuels
Friction stir welding
nuclear fuels
Spent fuels
disposal
Nuclear fuels
Copper
Welds
copper
welding
Hydrogen
shielding
Shielding
Oxides
hydrogen
ductility
Welding
Gases

All Science Journal Classification (ASJC) codes

  • Nuclear and High Energy Physics
  • Materials Science(all)
  • Nuclear Energy and Engineering

Cite this

Strain localization in copper canister FSW welds for spent nuclear fuel disposal. / Forsström, A.; Bossuyt, S.; Yagodzinskyy, Y.; Tsuzaki, K.; Hänninen, H.

In: Journal of Nuclear Materials, Vol. 523, 09.2019, p. 347-359.

Research output: Contribution to journalArticle

Forsström, A. ; Bossuyt, S. ; Yagodzinskyy, Y. ; Tsuzaki, K. ; Hänninen, H. / Strain localization in copper canister FSW welds for spent nuclear fuel disposal. In: Journal of Nuclear Materials. 2019 ; Vol. 523. pp. 347-359.
@article{8a9b995a2a4e4f0ba53f7674e992474e,
title = "Strain localization in copper canister FSW welds for spent nuclear fuel disposal",
abstract = "Spent nuclear fuel disposal in copper canisters in a deep geologic repository is planned in Finland and Sweden. The purpose of the copper shell is to perform as a ductile corrosion barrier to prevent radioactive substances from leaking into the environment. Therefore, the most important property of the copper shell, besides the good corrosion resistance, is its ductility. The copper canisters are sealed by friction stir welding (FSW), which results in strong welds when compared to the base materials, but the microstructural heterogeneity introduced by the welding may also lead to strain localization. Thus, the strain localization behavior of two different copper canister welds was studied by tensile tests in combination with digital image correlation (DIC). The main difference between the welds is the utilization of shielding gas to reduce oxidation during welding. The shielding gas improves the stability of the welding process, as well as reduces the number of oxide particles in the welds. It is known, that oxide particles are detrimental in copper in the presence of hydrogen. Therefore, the two welds were also thermally hydrogen charged to study hydrogen trapping in the weld material. Thermal desorption measurements (TDS) show that considerable hydrogen uptake occurs in the weld oxide zone, but it did not compromise the ductility of the copper welds in these tests. However, the DIC tests indicate considerably earlier strain localization on the retreating side of the new weld, welded with the shielding gas. This is attributed to differences in the initial state of the lid materials.",
author = "A. Forsstr{\"o}m and S. Bossuyt and Y. Yagodzinskyy and K. Tsuzaki and H. H{\"a}nninen",
year = "2019",
month = "9",
doi = "10.1016/j.jnucmat.2019.06.024",
language = "English",
volume = "523",
pages = "347--359",
journal = "Journal of Nuclear Materials",
issn = "0022-3115",
publisher = "Elsevier",

}

TY - JOUR

T1 - Strain localization in copper canister FSW welds for spent nuclear fuel disposal

AU - Forsström, A.

AU - Bossuyt, S.

AU - Yagodzinskyy, Y.

AU - Tsuzaki, K.

AU - Hänninen, H.

PY - 2019/9

Y1 - 2019/9

N2 - Spent nuclear fuel disposal in copper canisters in a deep geologic repository is planned in Finland and Sweden. The purpose of the copper shell is to perform as a ductile corrosion barrier to prevent radioactive substances from leaking into the environment. Therefore, the most important property of the copper shell, besides the good corrosion resistance, is its ductility. The copper canisters are sealed by friction stir welding (FSW), which results in strong welds when compared to the base materials, but the microstructural heterogeneity introduced by the welding may also lead to strain localization. Thus, the strain localization behavior of two different copper canister welds was studied by tensile tests in combination with digital image correlation (DIC). The main difference between the welds is the utilization of shielding gas to reduce oxidation during welding. The shielding gas improves the stability of the welding process, as well as reduces the number of oxide particles in the welds. It is known, that oxide particles are detrimental in copper in the presence of hydrogen. Therefore, the two welds were also thermally hydrogen charged to study hydrogen trapping in the weld material. Thermal desorption measurements (TDS) show that considerable hydrogen uptake occurs in the weld oxide zone, but it did not compromise the ductility of the copper welds in these tests. However, the DIC tests indicate considerably earlier strain localization on the retreating side of the new weld, welded with the shielding gas. This is attributed to differences in the initial state of the lid materials.

AB - Spent nuclear fuel disposal in copper canisters in a deep geologic repository is planned in Finland and Sweden. The purpose of the copper shell is to perform as a ductile corrosion barrier to prevent radioactive substances from leaking into the environment. Therefore, the most important property of the copper shell, besides the good corrosion resistance, is its ductility. The copper canisters are sealed by friction stir welding (FSW), which results in strong welds when compared to the base materials, but the microstructural heterogeneity introduced by the welding may also lead to strain localization. Thus, the strain localization behavior of two different copper canister welds was studied by tensile tests in combination with digital image correlation (DIC). The main difference between the welds is the utilization of shielding gas to reduce oxidation during welding. The shielding gas improves the stability of the welding process, as well as reduces the number of oxide particles in the welds. It is known, that oxide particles are detrimental in copper in the presence of hydrogen. Therefore, the two welds were also thermally hydrogen charged to study hydrogen trapping in the weld material. Thermal desorption measurements (TDS) show that considerable hydrogen uptake occurs in the weld oxide zone, but it did not compromise the ductility of the copper welds in these tests. However, the DIC tests indicate considerably earlier strain localization on the retreating side of the new weld, welded with the shielding gas. This is attributed to differences in the initial state of the lid materials.

UR - http://www.scopus.com/inward/record.url?scp=85067389600&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85067389600&partnerID=8YFLogxK

U2 - 10.1016/j.jnucmat.2019.06.024

DO - 10.1016/j.jnucmat.2019.06.024

M3 - Article

AN - SCOPUS:85067389600

VL - 523

SP - 347

EP - 359

JO - Journal of Nuclear Materials

JF - Journal of Nuclear Materials

SN - 0022-3115

ER -