Synthesis and microstructural evaluation of SiC-AlN composites

Keita Shirouzu, Yuki Nonaka, Mikinori Hotta, Naoya Enomoto, Junichi Hojo

Research output: Contribution to journalArticle

2 Citations (Scopus)

Abstract

High-density SiC-AlN composites were fabricated from powder mixtures (50:50 in mol) in 1900°C-2100°C temperature range by SPS process. SiC(0.3μm or 0.03μm) and AlN(1.1μm) were used as starting materials. The density of composite increased with increasing firing temperature. From the identification of crystal phase and the change of lattice constant, mixed phases of 3C(β-SiC)ss and 2H(α-SiC/AlN)ss were found at 1900°C and 2000°C, and only 2Hss was found at 2100°C The OM and EPMA observation indicated that SiC-rich regions (size:10-50μm) existed throughout SiC(0.3μm)-AlN composite because of aggregation of SiC powder. In SiC(0.03μm)-AlN composite, on the other hand, SiC-rich regions (size:submicron) and AlN-rich regions (size: approximately 1μm) existed on a microscopic level at 1900°C, whereras, it was confirmed from EPMA and SEM observation that homogeneous 2H(ss) formed with large grain-growth at 2100°C The microstructure of SiC(0.03μm)-AlN composite at 2000°C was analyzed to investigate more detailed compositional variation of solid solution. SEM-EDS observation indicated that 3C(ss), SiC-rich 2H(ss) and AlN-rich 2H(ss) existed in SiC(0.03μm)-AlN composite at 2000°C.

Original languageEnglish
Pages (from-to)193-196
Number of pages4
JournalKey Engineering Materials
Volume352
DOIs
Publication statusPublished - Oct 2 2007

    Fingerprint

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

Shirouzu, K., Nonaka, Y., Hotta, M., Enomoto, N., & Hojo, J. (2007). Synthesis and microstructural evaluation of SiC-AlN composites. Key Engineering Materials, 352, 193-196. https://doi.org/10.4028/0-87849-454-5.193