The effect of Si on the precipitates for nb bearing high-purity ferritic stainless steel

Masatoshi Ito, Yuma Honda, Masatoshi Aramaki, Yasushi Kato, Osamu Furukimi

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

The effect of Si on the precipitation of the Laves phase in high purity 17Cr-0.5Nb ferritic stainless steel was investigated. Precipitation was observed using a scanning electron microscope and transmission electron microscope. Quantitative analysis of the amount of precipitates as Laves phase was performed. The precipitation speed of the Laves phase and the equilibrium amount of precipitates of the Laves phase increased with the amount of Si. An Si peak was detected in the Laves phase in 0.5Si steel by EDX analysis. It was revealed that precipitation of the Laves phase is promoted and chemical composition of the Laves phase was changed by the addition of Si.

Original languageEnglish
Title of host publication65th ABM International Congress, 18th IFHTSE Congress and 1st TMS/ABM International Materials Congress 2010
Pages4213-4218
Number of pages6
Volume5
Publication statusPublished - 2010
Event65th ABM International Congress, 18th IFHTSE Congress and 1st TMS/ABM International Materials Congress 2010 - Rio de Janeiro, Brazil
Duration: Jul 26 2010Jul 30 2010

Other

Other65th ABM International Congress, 18th IFHTSE Congress and 1st TMS/ABM International Materials Congress 2010
CountryBrazil
CityRio de Janeiro
Period7/26/107/30/10

Fingerprint

Bearings (structural)
Ferritic steel
Precipitates
Electron microscopes
Stainless steel
Chemical analysis
Energy dispersive spectroscopy
Scanning
Steel

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials

Cite this

Ito, M., Honda, Y., Aramaki, M., Kato, Y., & Furukimi, O. (2010). The effect of Si on the precipitates for nb bearing high-purity ferritic stainless steel. In 65th ABM International Congress, 18th IFHTSE Congress and 1st TMS/ABM International Materials Congress 2010 (Vol. 5, pp. 4213-4218)

The effect of Si on the precipitates for nb bearing high-purity ferritic stainless steel. / Ito, Masatoshi; Honda, Yuma; Aramaki, Masatoshi; Kato, Yasushi; Furukimi, Osamu.

65th ABM International Congress, 18th IFHTSE Congress and 1st TMS/ABM International Materials Congress 2010. Vol. 5 2010. p. 4213-4218.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Ito, M, Honda, Y, Aramaki, M, Kato, Y & Furukimi, O 2010, The effect of Si on the precipitates for nb bearing high-purity ferritic stainless steel. in 65th ABM International Congress, 18th IFHTSE Congress and 1st TMS/ABM International Materials Congress 2010. vol. 5, pp. 4213-4218, 65th ABM International Congress, 18th IFHTSE Congress and 1st TMS/ABM International Materials Congress 2010, Rio de Janeiro, Brazil, 7/26/10.
Ito M, Honda Y, Aramaki M, Kato Y, Furukimi O. The effect of Si on the precipitates for nb bearing high-purity ferritic stainless steel. In 65th ABM International Congress, 18th IFHTSE Congress and 1st TMS/ABM International Materials Congress 2010. Vol. 5. 2010. p. 4213-4218
Ito, Masatoshi ; Honda, Yuma ; Aramaki, Masatoshi ; Kato, Yasushi ; Furukimi, Osamu. / The effect of Si on the precipitates for nb bearing high-purity ferritic stainless steel. 65th ABM International Congress, 18th IFHTSE Congress and 1st TMS/ABM International Materials Congress 2010. Vol. 5 2010. pp. 4213-4218
@inproceedings{468e3e8838ae463799d11f9eaee0d56b,
title = "The effect of Si on the precipitates for nb bearing high-purity ferritic stainless steel",
abstract = "The effect of Si on the precipitation of the Laves phase in high purity 17Cr-0.5Nb ferritic stainless steel was investigated. Precipitation was observed using a scanning electron microscope and transmission electron microscope. Quantitative analysis of the amount of precipitates as Laves phase was performed. The precipitation speed of the Laves phase and the equilibrium amount of precipitates of the Laves phase increased with the amount of Si. An Si peak was detected in the Laves phase in 0.5Si steel by EDX analysis. It was revealed that precipitation of the Laves phase is promoted and chemical composition of the Laves phase was changed by the addition of Si.",
author = "Masatoshi Ito and Yuma Honda and Masatoshi Aramaki and Yasushi Kato and Osamu Furukimi",
year = "2010",
language = "English",
isbn = "9781617820168",
volume = "5",
pages = "4213--4218",
booktitle = "65th ABM International Congress, 18th IFHTSE Congress and 1st TMS/ABM International Materials Congress 2010",

}

TY - GEN

T1 - The effect of Si on the precipitates for nb bearing high-purity ferritic stainless steel

AU - Ito, Masatoshi

AU - Honda, Yuma

AU - Aramaki, Masatoshi

AU - Kato, Yasushi

AU - Furukimi, Osamu

PY - 2010

Y1 - 2010

N2 - The effect of Si on the precipitation of the Laves phase in high purity 17Cr-0.5Nb ferritic stainless steel was investigated. Precipitation was observed using a scanning electron microscope and transmission electron microscope. Quantitative analysis of the amount of precipitates as Laves phase was performed. The precipitation speed of the Laves phase and the equilibrium amount of precipitates of the Laves phase increased with the amount of Si. An Si peak was detected in the Laves phase in 0.5Si steel by EDX analysis. It was revealed that precipitation of the Laves phase is promoted and chemical composition of the Laves phase was changed by the addition of Si.

AB - The effect of Si on the precipitation of the Laves phase in high purity 17Cr-0.5Nb ferritic stainless steel was investigated. Precipitation was observed using a scanning electron microscope and transmission electron microscope. Quantitative analysis of the amount of precipitates as Laves phase was performed. The precipitation speed of the Laves phase and the equilibrium amount of precipitates of the Laves phase increased with the amount of Si. An Si peak was detected in the Laves phase in 0.5Si steel by EDX analysis. It was revealed that precipitation of the Laves phase is promoted and chemical composition of the Laves phase was changed by the addition of Si.

UR - http://www.scopus.com/inward/record.url?scp=84893335730&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84893335730&partnerID=8YFLogxK

M3 - Conference contribution

AN - SCOPUS:84893335730

SN - 9781617820168

VL - 5

SP - 4213

EP - 4218

BT - 65th ABM International Congress, 18th IFHTSE Congress and 1st TMS/ABM International Materials Congress 2010

ER -