Thermal characteristics of a FeF3 cathode via conversion reaction in comparison with LiFePO4

Mingjiong Zhou, Liwei Zhao, Shigeto Okada, Jun Ichi Yamaki

Research output: Contribution to journalArticle

18 Citations (Scopus)

Abstract

The thermal stability of a FeF3 cathode via a conversion reaction was quantitatively studied using differential scanning calorimetry (DSC). Mixtures of charged and discharged FeF3 electrodes and electrolyte were measured by changing the ratio of electrode to electrolyte. A mild exothermic peak was observed at temperatures ranging from 210 to 380 °C for the mixtures of charged electrode and electrolyte even if the electrode/electrolyte ratio was changed. Moreover, the cycling depth had no effect on the thermal stability of the charged electrode in the electrolyte. For the mixtures of discharged electrode and electrolyte, exothermic reactions occurred in the range of 250-350 °C, which varied with the electrode/electrolyte ratio. Although the exothermic reactions of the mixtures varied with the electrode/electrolyte ratio, the thermal risk for both charged and discharged electrodes coexisted with the electrolyte appeared to be mainly due to electrolyte decomposition. By comparing the heat values of mixtures of the charged and discharged electrodes and electrolyte, the FeF3 electrodes in the electrolyte demonstrated better thermal stability than LiFePO4 electrodes at elevated temperatures.

Original languageEnglish
Pages (from-to)8110-8115
Number of pages6
JournalJournal of Power Sources
Volume196
Issue number19
DOIs
Publication statusPublished - Oct 1 2011

All Science Journal Classification (ASJC) codes

  • Renewable Energy, Sustainability and the Environment
  • Energy Engineering and Power Technology
  • Physical and Theoretical Chemistry
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Thermal characteristics of a FeF<sub>3</sub> cathode via conversion reaction in comparison with LiFePO<sub>4</sub>'. Together they form a unique fingerprint.

  • Cite this