Three-dimensional bicontinuous porous graphite generated in low temperature metallic liquid

Seung Geun Yu, Kunio Yubuta, Takeshi Wada, Hidemi Kato

Research output: Contribution to journalArticlepeer-review

40 Citations (Scopus)

Abstract

In this paper, three-dimensional bicontinuous porous graphite (3Dbp-graphite) with well-developed graphite structure is generated by dealloying in metallic melt at 1073 K in the low temperature region for synthesizing graphite. The N2 adsorption-desorption isotherm curves of 3Dbp-graphite show that the porous structure essentially consists of meso-macro pores. Its specific surface area and pore volume are 184.8 m2 g-1 and 0.84 cm3 g-1, respectively. These values are larger than the corresponding values of commercial acetylene black, which is widely used for energy devices. Both X-ray diffraction and the Raman spectra indicate that 3Dbp-graphite becomes more ordered when the graphitization process >2273 K. However, the specific surface area and total pore volume did not considerably decrease, indicating that porous graphite with extremely high electron conductivity and durability can be obtained by optimizing the dealloying and the following activation processes.

Original languageEnglish
Pages (from-to)403-410
Number of pages8
JournalCarbon
Volume96
DOIs
Publication statusPublished - Jan 2016
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Materials Science(all)

Fingerprint

Dive into the research topics of 'Three-dimensional bicontinuous porous graphite generated in low temperature metallic liquid'. Together they form a unique fingerprint.

Cite this