Tuning of the critical current in YBa2Cu3O 7-x thin films by controlling the size and density of Y 2O3 nanoislands on annealed SrTiO3 substrates

P. Mele, K. Matsumoto, T. Horide, O. Miura, A. Ichinose, M. Mukaida, Y. Yoshida, S. Horii

    Research output: Contribution to journalArticlepeer-review

    60 Citations (Scopus)

    Abstract

    We introduced high density columnar defects, as artificial pinning centres (APCs) for quantized vortices, into YBa2Cu3O7-x (YBCO) films during the film deposition procedure. APCs were introduced perpendicular to the film surface using nanosized Y2O3 islands prepared on SrTiO3(100) substrates by pulsed laser deposition. Varying the deposition parameters and the substrate annealing conditions allowed strong changes in the shape and density of the Y 2O3 islands to be induced. The best performance among the APC samples as compared to the pure YBCO film was obtained for that grown on the Y2O3-deposited substrate with five laser pulses, corresponding to 0.2 Y2O3 monolayers (ML). Even when the 0.2 ML APC films were prepared using the same deposition conditions, the columnar defects enhanced Jc at 77 K from 1.8 to 2.7 MA cm -2 (self-field) and from 0.06 to 0.10 MA cm-2 (H ≤ 5 T).

    Original languageEnglish
    Pages (from-to)44-50
    Number of pages7
    JournalSuperconductor Science and Technology
    Volume19
    Issue number1
    DOIs
    Publication statusPublished - Jan 1 2006

    All Science Journal Classification (ASJC) codes

    • Ceramics and Composites
    • Condensed Matter Physics
    • Metals and Alloys
    • Electrical and Electronic Engineering
    • Materials Chemistry

    Fingerprint

    Dive into the research topics of 'Tuning of the critical current in YBa<sub>2</sub>Cu<sub>3</sub>O <sub>7-x</sub> thin films by controlling the size and density of Y <sub>2</sub>O<sub>3</sub> nanoislands on annealed SrTiO<sub>3</sub> substrates'. Together they form a unique fingerprint.

    Cite this