高強度Al合金押出し材の超音波疲労特性

Translated title of the contribution: Ultrasonic Fatigue Properties of a High Strength Extruded Al Alloy

皮籠石 紀雄, 陳 強, 燕 怒, 王 清遠, 近藤 英二

Research output: Contribution to journalArticle

Abstract

In order to investigate the influence of loading frequency on the fatigue strength and fracture mechanism of a high strength Al alloy, ultrasonic fatigue tests were carried out for an extruded Al alloy 7075-T 6 and the results were compared with those of rotating bending fatigue tests. Fatigue strength of ultrasonic was higher than that of rotating bending. The crack initiation and the crack growth rate in ultrasonic fatigue were delayed compared with those of rotating bending fatigue. In case of ultrasonic fatigue, the direction of crack growth changed from tensile mode to shear mode and many voids were observed on the fracture surface in shear mode growth, whereas the crack propagated in tensile mode and striations were observed in rotating bending fatigue.
Original languageJapanese
Pages (from-to)1672-1677
Number of pages6
JournalNihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
Volume69
Issue number688
DOIs
Publication statusPublished - Dec 25 2003

Fingerprint

Ultrasonics
Fatigue of materials
Crack propagation
High strength alloys
Bending (deformation)
Crack initiation
Cracks
Fatigue strength

Cite this

高強度Al合金押出し材の超音波疲労特性. / 皮籠石紀雄; 陳強; 燕怒; 王清遠; 近藤英二.

In: Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, Vol. 69, No. 688, 25.12.2003, p. 1672-1677.

Research output: Contribution to journalArticle

@article{73bfd232cdb3443ebe326e945c34c207,
title = "高強度Al合金押出し材の超音波疲労特性",
abstract = "In order to investigate the influence of loading frequency on the fatigue strength and fracture mechanism of a high strength Al alloy, ultrasonic fatigue tests were carried out for an extruded Al alloy 7075-T 6 and the results were compared with those of rotating bending fatigue tests. Fatigue strength of ultrasonic was higher than that of rotating bending. The crack initiation and the crack growth rate in ultrasonic fatigue were delayed compared with those of rotating bending fatigue. In case of ultrasonic fatigue, the direction of crack growth changed from tensile mode to shear mode and many voids were observed on the fracture surface in shear mode growth, whereas the crack propagated in tensile mode and striations were observed in rotating bending fatigue.",
author = "紀雄 皮籠石 and 強 陳 and 怒 燕 and 清遠 王 and 英二 近藤",
year = "2003",
month = "12",
day = "25",
doi = "10.1299/kikaia.69.1672",
language = "Japanese",
volume = "69",
pages = "1672--1677",
journal = "Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A",
issn = "0387-5008",
publisher = "一般社団法人日本機械学会",
number = "688",

}

TY - JOUR

T1 - 高強度Al合金押出し材の超音波疲労特性

AU - 皮籠石, 紀雄

AU - 陳, 強

AU - 燕, 怒

AU - 王, 清遠

AU - 近藤, 英二

PY - 2003/12/25

Y1 - 2003/12/25

N2 - In order to investigate the influence of loading frequency on the fatigue strength and fracture mechanism of a high strength Al alloy, ultrasonic fatigue tests were carried out for an extruded Al alloy 7075-T 6 and the results were compared with those of rotating bending fatigue tests. Fatigue strength of ultrasonic was higher than that of rotating bending. The crack initiation and the crack growth rate in ultrasonic fatigue were delayed compared with those of rotating bending fatigue. In case of ultrasonic fatigue, the direction of crack growth changed from tensile mode to shear mode and many voids were observed on the fracture surface in shear mode growth, whereas the crack propagated in tensile mode and striations were observed in rotating bending fatigue.

AB - In order to investigate the influence of loading frequency on the fatigue strength and fracture mechanism of a high strength Al alloy, ultrasonic fatigue tests were carried out for an extruded Al alloy 7075-T 6 and the results were compared with those of rotating bending fatigue tests. Fatigue strength of ultrasonic was higher than that of rotating bending. The crack initiation and the crack growth rate in ultrasonic fatigue were delayed compared with those of rotating bending fatigue. In case of ultrasonic fatigue, the direction of crack growth changed from tensile mode to shear mode and many voids were observed on the fracture surface in shear mode growth, whereas the crack propagated in tensile mode and striations were observed in rotating bending fatigue.

U2 - 10.1299/kikaia.69.1672

DO - 10.1299/kikaia.69.1672

M3 - 記事

VL - 69

SP - 1672

EP - 1677

JO - Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A

JF - Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A

SN - 0387-5008

IS - 688

ER -