Viscosity of iron oxides containing multicomponent slags

Sohei Sukenaga, Tetsuya Nagahisa, Yoshiaki Gonda, Noritaka Saito, Junji Nakashima, Kunihiko Nakashima

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

Viscosity of the multicomponent slags which contain iron oxides (FeO and Fe203) have been measured by using rotating crucible method. In our experiments, we measured the viscosity from 1673 to 1873K under air. Effects of the basicity and the iron oxide additions on the viscosity were clarified. Temperature dependences of the viscosity for the slags were expressed by Arrhenius type equation in the present study. Theviscosity of the slags decreased linearly with increasing the basicity (CaO/Si02). Also, the viscosity of the slags decreased with increasing the additive content of iron oxides. The decreases in viscosity with the addition of iron oxides are larger in thelower basicity system than those in the higher basicity system. The results of chemical analysis for the slag samples after viscosity measurements indicated that iron oxide in these slags has mainly existed as Fe 203 (Fe3+). Therefore,we calculated the parameter of αfe203 which was a coefficientrelated to the amphoteric behavior of fe203 in accordance with the Iida's model. The parameter of αfe203 increased with decreasing the bacisity. The results suggested that Fe20 3 had a greater tendency to behave as a basic oxide in the lower bacisity system than in the higher basicitysystem. It is therefore that the decreases in viscosity with addition of the iron oxides are considered to be large in lower basicity system.

Original languageEnglish
Pages (from-to)469-474
Number of pages6
JournalTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
Volume96
Issue number8
DOIs
Publication statusPublished - Oct 19 2010

Fingerprint

slags
Iron oxides
iron oxides
Slags
Alkalinity
Viscosity
viscosity
Crucibles
Viscosity measurement
ferric oxide
Oxides
crucibles
chemical analysis
tendencies
temperature dependence
oxides
Air
Chemical analysis
air

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Physical and Theoretical Chemistry
  • Metals and Alloys
  • Materials Chemistry

Cite this

Viscosity of iron oxides containing multicomponent slags. / Sukenaga, Sohei; Nagahisa, Tetsuya; Gonda, Yoshiaki; Saito, Noritaka; Nakashima, Junji; Nakashima, Kunihiko.

In: Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, Vol. 96, No. 8, 19.10.2010, p. 469-474.

Research output: Contribution to journalArticle

Sukenaga, Sohei ; Nagahisa, Tetsuya ; Gonda, Yoshiaki ; Saito, Noritaka ; Nakashima, Junji ; Nakashima, Kunihiko. / Viscosity of iron oxides containing multicomponent slags. In: Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan. 2010 ; Vol. 96, No. 8. pp. 469-474.
@article{abbb8e079d214862b20aad004a171a7c,
title = "Viscosity of iron oxides containing multicomponent slags",
abstract = "Viscosity of the multicomponent slags which contain iron oxides (FeO and Fe203) have been measured by using rotating crucible method. In our experiments, we measured the viscosity from 1673 to 1873K under air. Effects of the basicity and the iron oxide additions on the viscosity were clarified. Temperature dependences of the viscosity for the slags were expressed by Arrhenius type equation in the present study. Theviscosity of the slags decreased linearly with increasing the basicity (CaO/Si02). Also, the viscosity of the slags decreased with increasing the additive content of iron oxides. The decreases in viscosity with the addition of iron oxides are larger in thelower basicity system than those in the higher basicity system. The results of chemical analysis for the slag samples after viscosity measurements indicated that iron oxide in these slags has mainly existed as Fe 203 (Fe3+). Therefore,we calculated the parameter of αfe203 which was a coefficientrelated to the amphoteric behavior of fe203 in accordance with the Iida's model. The parameter of αfe203 increased with decreasing the bacisity. The results suggested that Fe20 3 had a greater tendency to behave as a basic oxide in the lower bacisity system than in the higher basicitysystem. It is therefore that the decreases in viscosity with addition of the iron oxides are considered to be large in lower basicity system.",
author = "Sohei Sukenaga and Tetsuya Nagahisa and Yoshiaki Gonda and Noritaka Saito and Junji Nakashima and Kunihiko Nakashima",
year = "2010",
month = "10",
day = "19",
doi = "10.2355/tetsutohagane.96.469",
language = "English",
volume = "96",
pages = "469--474",
journal = "Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan",
issn = "0021-1575",
publisher = "一般社団法人 日本鉄鋼協会",
number = "8",

}

TY - JOUR

T1 - Viscosity of iron oxides containing multicomponent slags

AU - Sukenaga, Sohei

AU - Nagahisa, Tetsuya

AU - Gonda, Yoshiaki

AU - Saito, Noritaka

AU - Nakashima, Junji

AU - Nakashima, Kunihiko

PY - 2010/10/19

Y1 - 2010/10/19

N2 - Viscosity of the multicomponent slags which contain iron oxides (FeO and Fe203) have been measured by using rotating crucible method. In our experiments, we measured the viscosity from 1673 to 1873K under air. Effects of the basicity and the iron oxide additions on the viscosity were clarified. Temperature dependences of the viscosity for the slags were expressed by Arrhenius type equation in the present study. Theviscosity of the slags decreased linearly with increasing the basicity (CaO/Si02). Also, the viscosity of the slags decreased with increasing the additive content of iron oxides. The decreases in viscosity with the addition of iron oxides are larger in thelower basicity system than those in the higher basicity system. The results of chemical analysis for the slag samples after viscosity measurements indicated that iron oxide in these slags has mainly existed as Fe 203 (Fe3+). Therefore,we calculated the parameter of αfe203 which was a coefficientrelated to the amphoteric behavior of fe203 in accordance with the Iida's model. The parameter of αfe203 increased with decreasing the bacisity. The results suggested that Fe20 3 had a greater tendency to behave as a basic oxide in the lower bacisity system than in the higher basicitysystem. It is therefore that the decreases in viscosity with addition of the iron oxides are considered to be large in lower basicity system.

AB - Viscosity of the multicomponent slags which contain iron oxides (FeO and Fe203) have been measured by using rotating crucible method. In our experiments, we measured the viscosity from 1673 to 1873K under air. Effects of the basicity and the iron oxide additions on the viscosity were clarified. Temperature dependences of the viscosity for the slags were expressed by Arrhenius type equation in the present study. Theviscosity of the slags decreased linearly with increasing the basicity (CaO/Si02). Also, the viscosity of the slags decreased with increasing the additive content of iron oxides. The decreases in viscosity with the addition of iron oxides are larger in thelower basicity system than those in the higher basicity system. The results of chemical analysis for the slag samples after viscosity measurements indicated that iron oxide in these slags has mainly existed as Fe 203 (Fe3+). Therefore,we calculated the parameter of αfe203 which was a coefficientrelated to the amphoteric behavior of fe203 in accordance with the Iida's model. The parameter of αfe203 increased with decreasing the bacisity. The results suggested that Fe20 3 had a greater tendency to behave as a basic oxide in the lower bacisity system than in the higher basicitysystem. It is therefore that the decreases in viscosity with addition of the iron oxides are considered to be large in lower basicity system.

UR - http://www.scopus.com/inward/record.url?scp=77957884266&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=77957884266&partnerID=8YFLogxK

U2 - 10.2355/tetsutohagane.96.469

DO - 10.2355/tetsutohagane.96.469

M3 - Article

VL - 96

SP - 469

EP - 474

JO - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

JF - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

SN - 0021-1575

IS - 8

ER -