Wear resistance and tribological features of pure aluminum and Al-Al2O3 composites consolidated by high-pressure torsion

Kaveh Edalati, Maki Ashida, Zenji Horita, Toshiaki Matsui, Hirotaka Kato

Research output: Contribution to journalArticlepeer-review

57 Citations (Scopus)


Ultrafine-grained pure Al and Al-based composites with 10 and 20vol% of Al2O3 were produced by cold consolidation of powders using high-pressure torsion (HPT). Ball-on-disc wear resistance of Al was improved by HPT when compared to its coarse-grained counterpart processed with H24 treatment (cold rolling followed by low-temperature annealing). Wear width decreased but wear depth and wear volume increased with the addition of Al2O3 to the Al matrix. The wear mechanism was mainly due to adhesion in Al and Al-Al2O3 composites. It was found that the variation of wear width can be represented by a unique function of the ratio of load/hardness in consistency with the Reye's hypothesis and the Holm and Archard relationships. However, the variation of wear depth was inconsistent with the hardness variations.

Original languageEnglish
Pages (from-to)83-89
Number of pages7
Issue number1-2
Publication statusPublished - Feb 15 2014

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry


Dive into the research topics of 'Wear resistance and tribological features of pure aluminum and Al-Al<sub>2</sub>O<sub>3</sub> composites consolidated by high-pressure torsion'. Together they form a unique fingerprint.

Cite this