Wettability of Al2O3 Substrate by Liquid Iron—Effects of Oxygen in Liquid Iron and Purity of Al2O3 Substrate—

Kunihiko Nakashima, Katsumi Mori, Kenji Takihira, Nobuya Shinozaki

    Research output: Contribution to journalArticlepeer-review

    36 Citations (Scopus)

    Abstract

    The interfacial properties between liquid Fe-O alloy and alumina substrates with different purities, 99.9% and 96% Al2O3, were measured by the sessile drop method. The interfaces of samples were examined by SEM and EPMA after the experiment. It was found that the surface tension decreased with increasing oxygen concentration in the iron for both substrates. The contact angle of 99.9% Al2O3 abruptly increased with increasing oxygen concentration at lower oxygen concentrations. These phenomena were attributed to the dissociation of Al2O3. Moreover, at higher oxygen concentration, the formation of the dense hercynite was observed at the Fe-O/Al2O3 interface, the contact angle slightly decreased with increasing oxygen concentration. For 96% Al2O3, a Ca- or Mg-rich layer was observed at the interface at a lower oxygen concentration, the contact angle abruptly increased with increasing oxygen concentration. Whereas, at higher oxygen concentrations, the contact angle rapidly decreased with increasing oxygen concentration. Under these conditions, the formation of hercynite and the penetration of iron into the grain boundaries of Al2O3 substrates were observed.

    Original languageEnglish
    Pages (from-to)918-926
    Number of pages9
    JournalMaterials Transactions, JIM
    Volume33
    Issue number10
    DOIs
    Publication statusPublished - Jan 1 1992