Wetting and penetration behavior of calcium ferrite melts to sintered hematite

Kunihiko Nakashima, Noritaka Saito, Shurisuke Shinozaki, Ryuji Tanaka, Takayuki Maeda, Masakata Shimizu, Katsumi Mori

Research output: Contribution to journalArticle

24 Citations (Scopus)

Abstract

Effects of adding SiO2 or Al2O3 on the wetting and penetration characteristics of calcium ferrite melts, CaO · Fe2O3 (CF) and CaO · Fe2O 3(CF2), to sintered hematite substrate have been examined. And the wetting and penetration characteristics were discussed from the viewpoints of the relation to the viscosity and surface tension of calcium ferrite melts. The effects of the addition of calcium ferrite slag with SiO 2 or Al2O3 on the strength of sintered hematite pellets were also examined. The slag tablets of CF2-based slag neither melt completely nor spread uniformly on the hematite substrate at the experimental temperature at 1 300°C in this study. The wettability of CF-based slag melts on sintered hematite substrate was improved by the addition of Si2 or Al2O3, and the spreading rate was increased with increasing the value of 77/7 (viscosity/surface tension of slag melts). The penetration of CF-based slag melts into sintered hematite substrate was depressed by the addition of SiO2 or Al2O 3, and the penetration depth was increased with increasing the value of η/γ surface tension/ viscosity of slag melts). The sintered hematite pellet with CF-5 mass%Al2O3 slag sintered at 1 200°C had the highest compressive strength in this study. Because the liquidus temperature of CF slag is decreased to about 1 200°C by adding 5 mass% Al2O3, and the sufficient amount of liquid phase, which has the appropriate wetting and penetrating characteristics controlled by the surface tension and the viscosity, as a binder was formed.

Original languageEnglish
Pages (from-to)2052-2056
Number of pages5
Journalisij international
Volume44
Issue number12
DOIs
Publication statusPublished - Jan 1 2004

Fingerprint

Hematite
Slags
Ferrite
Wetting
Calcium
Surface tension
Viscosity
Substrates
ferric oxide
Tablets
Compressive strength
Binders
Temperature
Liquids

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Cite this

Wetting and penetration behavior of calcium ferrite melts to sintered hematite. / Nakashima, Kunihiko; Saito, Noritaka; Shinozaki, Shurisuke; Tanaka, Ryuji; Maeda, Takayuki; Shimizu, Masakata; Mori, Katsumi.

In: isij international, Vol. 44, No. 12, 01.01.2004, p. 2052-2056.

Research output: Contribution to journalArticle

Nakashima, Kunihiko ; Saito, Noritaka ; Shinozaki, Shurisuke ; Tanaka, Ryuji ; Maeda, Takayuki ; Shimizu, Masakata ; Mori, Katsumi. / Wetting and penetration behavior of calcium ferrite melts to sintered hematite. In: isij international. 2004 ; Vol. 44, No. 12. pp. 2052-2056.
@article{438d5bb4b43546479399e428b14aa95c,
title = "Wetting and penetration behavior of calcium ferrite melts to sintered hematite",
abstract = "Effects of adding SiO2 or Al2O3 on the wetting and penetration characteristics of calcium ferrite melts, CaO · Fe2O3 (CF) and CaO · Fe2O 3(CF2), to sintered hematite substrate have been examined. And the wetting and penetration characteristics were discussed from the viewpoints of the relation to the viscosity and surface tension of calcium ferrite melts. The effects of the addition of calcium ferrite slag with SiO 2 or Al2O3 on the strength of sintered hematite pellets were also examined. The slag tablets of CF2-based slag neither melt completely nor spread uniformly on the hematite substrate at the experimental temperature at 1 300°C in this study. The wettability of CF-based slag melts on sintered hematite substrate was improved by the addition of Si2 or Al2O3, and the spreading rate was increased with increasing the value of 77/7 (viscosity/surface tension of slag melts). The penetration of CF-based slag melts into sintered hematite substrate was depressed by the addition of SiO2 or Al2O 3, and the penetration depth was increased with increasing the value of η/γ surface tension/ viscosity of slag melts). The sintered hematite pellet with CF-5 mass{\%}Al2O3 slag sintered at 1 200°C had the highest compressive strength in this study. Because the liquidus temperature of CF slag is decreased to about 1 200°C by adding 5 mass{\%} Al2O3, and the sufficient amount of liquid phase, which has the appropriate wetting and penetrating characteristics controlled by the surface tension and the viscosity, as a binder was formed.",
author = "Kunihiko Nakashima and Noritaka Saito and Shurisuke Shinozaki and Ryuji Tanaka and Takayuki Maeda and Masakata Shimizu and Katsumi Mori",
year = "2004",
month = "1",
day = "1",
doi = "10.2355/isijinternational.44.2052",
language = "English",
volume = "44",
pages = "2052--2056",
journal = "ISIJ International",
issn = "0915-1559",
publisher = "Iron and Steel Institute of Japan",
number = "12",

}

TY - JOUR

T1 - Wetting and penetration behavior of calcium ferrite melts to sintered hematite

AU - Nakashima, Kunihiko

AU - Saito, Noritaka

AU - Shinozaki, Shurisuke

AU - Tanaka, Ryuji

AU - Maeda, Takayuki

AU - Shimizu, Masakata

AU - Mori, Katsumi

PY - 2004/1/1

Y1 - 2004/1/1

N2 - Effects of adding SiO2 or Al2O3 on the wetting and penetration characteristics of calcium ferrite melts, CaO · Fe2O3 (CF) and CaO · Fe2O 3(CF2), to sintered hematite substrate have been examined. And the wetting and penetration characteristics were discussed from the viewpoints of the relation to the viscosity and surface tension of calcium ferrite melts. The effects of the addition of calcium ferrite slag with SiO 2 or Al2O3 on the strength of sintered hematite pellets were also examined. The slag tablets of CF2-based slag neither melt completely nor spread uniformly on the hematite substrate at the experimental temperature at 1 300°C in this study. The wettability of CF-based slag melts on sintered hematite substrate was improved by the addition of Si2 or Al2O3, and the spreading rate was increased with increasing the value of 77/7 (viscosity/surface tension of slag melts). The penetration of CF-based slag melts into sintered hematite substrate was depressed by the addition of SiO2 or Al2O 3, and the penetration depth was increased with increasing the value of η/γ surface tension/ viscosity of slag melts). The sintered hematite pellet with CF-5 mass%Al2O3 slag sintered at 1 200°C had the highest compressive strength in this study. Because the liquidus temperature of CF slag is decreased to about 1 200°C by adding 5 mass% Al2O3, and the sufficient amount of liquid phase, which has the appropriate wetting and penetrating characteristics controlled by the surface tension and the viscosity, as a binder was formed.

AB - Effects of adding SiO2 or Al2O3 on the wetting and penetration characteristics of calcium ferrite melts, CaO · Fe2O3 (CF) and CaO · Fe2O 3(CF2), to sintered hematite substrate have been examined. And the wetting and penetration characteristics were discussed from the viewpoints of the relation to the viscosity and surface tension of calcium ferrite melts. The effects of the addition of calcium ferrite slag with SiO 2 or Al2O3 on the strength of sintered hematite pellets were also examined. The slag tablets of CF2-based slag neither melt completely nor spread uniformly on the hematite substrate at the experimental temperature at 1 300°C in this study. The wettability of CF-based slag melts on sintered hematite substrate was improved by the addition of Si2 or Al2O3, and the spreading rate was increased with increasing the value of 77/7 (viscosity/surface tension of slag melts). The penetration of CF-based slag melts into sintered hematite substrate was depressed by the addition of SiO2 or Al2O 3, and the penetration depth was increased with increasing the value of η/γ surface tension/ viscosity of slag melts). The sintered hematite pellet with CF-5 mass%Al2O3 slag sintered at 1 200°C had the highest compressive strength in this study. Because the liquidus temperature of CF slag is decreased to about 1 200°C by adding 5 mass% Al2O3, and the sufficient amount of liquid phase, which has the appropriate wetting and penetrating characteristics controlled by the surface tension and the viscosity, as a binder was formed.

UR - http://www.scopus.com/inward/record.url?scp=13444273353&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=13444273353&partnerID=8YFLogxK

U2 - 10.2355/isijinternational.44.2052

DO - 10.2355/isijinternational.44.2052

M3 - Article

AN - SCOPUS:13444273353

VL - 44

SP - 2052

EP - 2056

JO - ISIJ International

JF - ISIJ International

SN - 0915-1559

IS - 12

ER -