YBa2Cu3O7-x + YSZ mixed films with enhanced critical current densities in magnetic field

P. Mele, K. Matsumoto, T. Horide, A. Ichinose, M. Mukaida, Y. Yoshida, S. Horii

    Research output: Contribution to journalArticlepeer-review

    1 Citation (Scopus)

    Abstract

    YBa2Cu3O7-x + YSZ (YBCO + YSZ) mixed films were prepared on SrTiO3/MgO substrates by pulsed laser deposition (PLD) from a YBCO target with thin YSZ sector on the top of the target. In comparison with a pure YBCO film, the Jc at 77 K for mixed YBCO + YSZ thin film was enhanced from 1.46 MA/cm2 to 1.95 MA/cm2 (self-field) and from 0.09 MA/cm2 to 0.28 MA/cm2 (B∥c, B = 5 T) even when both films were prepared on the same deposition conditions. In the YSZ-added sample, the angular dependence of Jc shows a broad peak at B∥c, due to the flux pinning by c-axis correlated defects. Consistently, elongated nanorods grown in the direction parallel to c-axis were observed in cross-sectional TEM images.

    Original languageEnglish
    Pages (from-to)653-656
    Number of pages4
    JournalPhysica C: Superconductivity and its applications
    Volume463-465
    Issue numberSUPPL.
    DOIs
    Publication statusPublished - Oct 1 2007

    All Science Journal Classification (ASJC) codes

    • Electronic, Optical and Magnetic Materials
    • Condensed Matter Physics
    • Energy Engineering and Power Technology
    • Electrical and Electronic Engineering

    Fingerprint

    Dive into the research topics of 'YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-x</sub> + YSZ mixed films with enhanced critical current densities in magnetic field'. Together they form a unique fingerprint.

    Cite this