高強度Al合金押出し材の超音波疲労特性

皮籠石 紀雄, 陳 強, 燕 怒, 王 清遠, 近藤 英二

研究成果: ジャーナルへの寄稿学術誌査読

抄録

In order to investigate the influence of loading frequency on the fatigue strength and fracture mechanism of a high strength Al alloy, ultrasonic fatigue tests were carried out for an extruded Al alloy 7075-T 6 and the results were compared with those of rotating bending fatigue tests. Fatigue strength of ultrasonic was higher than that of rotating bending. The crack initiation and the crack growth rate in ultrasonic fatigue were delayed compared with those of rotating bending fatigue. In case of ultrasonic fatigue, the direction of crack growth changed from tensile mode to shear mode and many voids were observed on the fracture surface in shear mode growth, whereas the crack propagated in tensile mode and striations were observed in rotating bending fatigue.
寄稿の翻訳タイトルUltrasonic Fatigue Properties of a High Strength Extruded Al Alloy
本文言語日本語
ページ(範囲)1672-1677
ページ数6
ジャーナルNihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
69
688
DOI
出版ステータス出版済み - 12月 25 2003

フィンガープリント

「高強度Al合金押出し材の超音波疲労特性」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル