512 熱衝撃によるヒートクラック発生条件の定量的評価(OS9-2 衝撃と種々の測定法,OS9 実験力学における新たな試み)

園田 晃大, 柏木 卓, 濱田 繁, 野口 博司

研究成果: Contribution to journalArticle

抄録

In this paper, we have proposed an evaluation method for the initiation conditions of heat crack under thermal shock using the tensile test of a notched specimen. In some materials, such as hot rolling rolls and dies for aluminum die-casting, there is a problem of heat crack initiation, and the evaluation of heat crack resistance using test pieces was difficult until now. The thermal stress and stress gradient that occurred in such material were analyzed by the finite element method (FEM). The maximum stress when tensile stress was applied to the material with a notch was compared to the stress gradient of the thermal stress. As a result, the quantitative evaluation during the initiation conditions of a heat crack for materials became possible.
寄稿の翻訳タイトル512 Quantitative Evaluation of Heat Crack Initiation Condition Under Thermal Shock
本文言語Japanese
ページ(範囲)361-362
ページ数2
ジャーナルM&M材料力学カンファレンス
2007
0
DOI
出版ステータス出版済み - 2007

フィンガープリント 「512 熱衝撃によるヒートクラック発生条件の定量的評価(OS9-2 衝撃と種々の測定法,OS9 実験力学における新たな試み)」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル