A non-microstructural crack formation model for understanding fatigue life degradation in shot peened carbon steel under LCF loading

Jong Cheon Kim, Seong Kyun Cheong, Hiroshi Noguchi

研究成果: Contribution to journalArticle査読

3 被引用数 (Scopus)

抄録

The present paper was based on the experimental investigation from the previous results that analyzed the residual stress relaxation and its fatigue behavior in shot-peened (SP) specimen during fatigue loading Kim et al. (2013) [12,10]. Here, the non-microstructural crack formation model was proposed to understand fatigue life degradation of SP carbon steel under LCF loading. When the applied stress exceeded the yield strength of the original material from the previous results, the SP specimen showed a shorter fatigue life as compared to the specimen without SP. To demonstrate the empirical model, the fatigue crack initiation and propagation in no SP specimens were observed by the plastic replication method at the LCF loading. The results showed the following: (i) remarked residual stress relaxation occurred under LCF loading which leads to the ability to have a significant influence on the degradation of fatigue life in the SP specimen; (ii) the existing microcracks on the treated surface caused earlier fatigue failure owing to crack formation, which was not influenced by microstructural effects. This presentation will discuss the non-microstructural crack formation in detail and suggest a mechanism for the fatigue life degradation.

本文言語英語
ページ(範囲)110-117
ページ数8
ジャーナルInternational Journal of Fatigue
63
DOI
出版ステータス出版済み - 6 2014

All Science Journal Classification (ASJC) codes

  • モデリングとシミュレーション
  • 材料科学(全般)
  • 材料力学
  • 機械工学
  • 産業および生産工学

フィンガープリント

「A non-microstructural crack formation model for understanding fatigue life degradation in shot peened carbon steel under LCF loading」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル