A novel electric power generation under uniform temperature environment using poly-crystalline Ba8AuxSi46-x clathrate

Shinji Munetoh, Yuuki Osakabe, Keita Yamasoto, Jyunpei Iwanaga, Hideshi Miura, Osamu Furukimi

研究成果: ジャーナルへの寄稿記事

抄録

Poly-crystalline Ba8AuxSi46-xclathrate with p-n junction was synthesized for electric power generation from heat under no temperature difference. The n-type Ba8Au4.5Si41.5 and the p-type Ba8Au5.5Si40.5 powder were stacked in the graphite die and sintered by a Spark Plasma Sintering (SPS) method at 1073 K for 5 min with pressure of 50 MPa. The Au composition of Ba8Au4.5Si41.5 and Ba8Au5.5Si40.5 side in the sintered sample were Ba7.8Au4.2Si41.8 and Ba7.8Au5.2Si40.8, respectively. It was found that the Au composition was gradually changed near the interface with thickness of around 500 micrometers. Electric power generation test under no temperature difference was performed by using the sample cut to contain the interface of two layers. The electric power increased by only heating and the maximum voltage can be observed around 2 mV at 773 K. These results suggested that electron excitation occurred near the n/p interface and generated electrons and holes diffuse to n-type and p-type semiconductor side, respectively.

元の言語英語
ページ(範囲)471-474
ページ数4
ジャーナルFuntai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
64
発行部数8
DOI
出版物ステータス出版済み - 8 1 2017

Fingerprint

Electric power generation
Crystalline materials
Spark plasma sintering
Graphite
Electrons
Chemical analysis
Powders
Semiconductor materials
Heating
Temperature
Electric potential
Hot Temperature

All Science Journal Classification (ASJC) codes

  • Mechanical Engineering
  • Industrial and Manufacturing Engineering
  • Metals and Alloys
  • Materials Chemistry

これを引用

A novel electric power generation under uniform temperature environment using poly-crystalline Ba8AuxSi46-x clathrate. / Munetoh, Shinji; Osakabe, Yuuki; Yamasoto, Keita; Iwanaga, Jyunpei; Miura, Hideshi; Furukimi, Osamu.

:: Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy, 巻 64, 番号 8, 01.08.2017, p. 471-474.

研究成果: ジャーナルへの寄稿記事

@article{c7ee779e35764713b68e86b5841cf730,
title = "A novel electric power generation under uniform temperature environment using poly-crystalline Ba8AuxSi46-x clathrate",
abstract = "Poly-crystalline Ba8AuxSi46-xclathrate with p-n junction was synthesized for electric power generation from heat under no temperature difference. The n-type Ba8Au4.5Si41.5 and the p-type Ba8Au5.5Si40.5 powder were stacked in the graphite die and sintered by a Spark Plasma Sintering (SPS) method at 1073 K for 5 min with pressure of 50 MPa. The Au composition of Ba8Au4.5Si41.5 and Ba8Au5.5Si40.5 side in the sintered sample were Ba7.8Au4.2Si41.8 and Ba7.8Au5.2Si40.8, respectively. It was found that the Au composition was gradually changed near the interface with thickness of around 500 micrometers. Electric power generation test under no temperature difference was performed by using the sample cut to contain the interface of two layers. The electric power increased by only heating and the maximum voltage can be observed around 2 mV at 773 K. These results suggested that electron excitation occurred near the n/p interface and generated electrons and holes diffuse to n-type and p-type semiconductor side, respectively.",
author = "Shinji Munetoh and Yuuki Osakabe and Keita Yamasoto and Jyunpei Iwanaga and Hideshi Miura and Osamu Furukimi",
year = "2017",
month = "8",
day = "1",
doi = "10.2497/jjspm.64.471",
language = "English",
volume = "64",
pages = "471--474",
journal = "Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy",
issn = "0532-8799",
publisher = "Japan Society of Powder and Powder Metallurgy",
number = "8",

}

TY - JOUR

T1 - A novel electric power generation under uniform temperature environment using poly-crystalline Ba8AuxSi46-x clathrate

AU - Munetoh, Shinji

AU - Osakabe, Yuuki

AU - Yamasoto, Keita

AU - Iwanaga, Jyunpei

AU - Miura, Hideshi

AU - Furukimi, Osamu

PY - 2017/8/1

Y1 - 2017/8/1

N2 - Poly-crystalline Ba8AuxSi46-xclathrate with p-n junction was synthesized for electric power generation from heat under no temperature difference. The n-type Ba8Au4.5Si41.5 and the p-type Ba8Au5.5Si40.5 powder were stacked in the graphite die and sintered by a Spark Plasma Sintering (SPS) method at 1073 K for 5 min with pressure of 50 MPa. The Au composition of Ba8Au4.5Si41.5 and Ba8Au5.5Si40.5 side in the sintered sample were Ba7.8Au4.2Si41.8 and Ba7.8Au5.2Si40.8, respectively. It was found that the Au composition was gradually changed near the interface with thickness of around 500 micrometers. Electric power generation test under no temperature difference was performed by using the sample cut to contain the interface of two layers. The electric power increased by only heating and the maximum voltage can be observed around 2 mV at 773 K. These results suggested that electron excitation occurred near the n/p interface and generated electrons and holes diffuse to n-type and p-type semiconductor side, respectively.

AB - Poly-crystalline Ba8AuxSi46-xclathrate with p-n junction was synthesized for electric power generation from heat under no temperature difference. The n-type Ba8Au4.5Si41.5 and the p-type Ba8Au5.5Si40.5 powder were stacked in the graphite die and sintered by a Spark Plasma Sintering (SPS) method at 1073 K for 5 min with pressure of 50 MPa. The Au composition of Ba8Au4.5Si41.5 and Ba8Au5.5Si40.5 side in the sintered sample were Ba7.8Au4.2Si41.8 and Ba7.8Au5.2Si40.8, respectively. It was found that the Au composition was gradually changed near the interface with thickness of around 500 micrometers. Electric power generation test under no temperature difference was performed by using the sample cut to contain the interface of two layers. The electric power increased by only heating and the maximum voltage can be observed around 2 mV at 773 K. These results suggested that electron excitation occurred near the n/p interface and generated electrons and holes diffuse to n-type and p-type semiconductor side, respectively.

UR - http://www.scopus.com/inward/record.url?scp=85028918534&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85028918534&partnerID=8YFLogxK

U2 - 10.2497/jjspm.64.471

DO - 10.2497/jjspm.64.471

M3 - Article

VL - 64

SP - 471

EP - 474

JO - Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy

JF - Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy

SN - 0532-8799

IS - 8

ER -