Accommodation of uranium into the garnet structure

Sergey V. Yudintsev, Marya I. Lapina, Alexander G. Ptashkin, Tatiana S. Ioudintseva, Satoshi Utsunomiya, Lumin M. Wang, Rodney C. Ewing

研究成果: Contribution to journalArticle査読

29 被引用数 (Scopus)

抄録

One promising host for actinide wastes is garnet-type phases of general formula AVIII3BVI2[XO4]3. To determine the isomorphic capacity of garnet for uranium, CaO - Fe2O3 - Al2O3 - SiO2 - ZrO2 - Gd2O3 - UO2 system was studied. Experiments were performed in air medium at 1400 - 1500°C and 1 atm. The garnets have high capacity for Gd and Zr, while incorporation of U was found to be greatly dependent on the phase composition. Uranium content decreased from 18 wt.% in Ca-Zr-Fe garnet to 0.6 wt.% in Si-doped phases. Heavy ion irradiation (1.0 MeV Kr++) experiments were carried out for a garnet with maximal U content, (Ca2,7U0,3) VIII(Zr1,7Fe0,3) VI(Al1,1Fe1,9)IV O12. Amorphization dose of the phase was equal to 1.63×1014 ions/cm2 that is close to the other actinide hosts, such as pyrochlore Gd2Ti2O7.

本文言語英語
ページ(範囲)477-480
ページ数4
ジャーナルMaterials Research Society Symposium - Proceedings
713
DOI
出版ステータス出版済み - 2002
外部発表はい

All Science Journal Classification (ASJC) codes

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Accommodation of uranium into the garnet structure」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル