Experiments were conducted to evaluate the utility of a new processing procedure developed for Mg-based alloys in which samples are subjected to a two-step processing route of extrusion followed by equal-channel angular pressing (designated as EX-ECAP). The experiments were conducted using a Mg-0.6 wt pct Zr alloy and, for comparison purposes, samples of pure Mg. It is shown that the potential for successfully using ECAP increases in both materials when adopting the EX-ECAP procedure. For the Mg-Zr alloy, the use of EX-ECAP produces a grain size of ∼1.4 μm when the pressing is undertaken at 573 K. By contrast, using EX-ECAP with pure Mg at 573 K produces a grain size of ∼26 μm. Tensile testing of the Mg-Zr alloy at 523 and 573 K after processing by EX-ECAP revealed the occurrence of significantly enhanced ductilities with maximum elongations of ∼300 to 400 pct.
|ジャーナル||Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science|
|出版物ステータス||出版済み - 1 1 2004|
All Science Journal Classification (ASJC) codes
- Condensed Matter Physics
- Mechanics of Materials
- Metals and Alloys