Activated carbon fibers prepared from quinoline and isoquinoline pitches

Isao Mochida, Kay Hyeok An, Yozo Korai, Takashi Kojima, Makoto Komatsu, Masaaki Yoshikawa

研究成果: Contribution to journalArticle査読

1 被引用数 (Scopus)

抄録

Nitrogen enriched activated carbon fibers(ACFs) were prepared from isotropic quinoline and isoquinoline pitches produced by the catalytic action of HF/BF3 through spinning, stabilization, carbonization, and oxidative activation. The pitches exhibited excellent spinnability, and the resultant fibers had mechanical properties comparable to those of commercial fibers. The surface areas and nitrogen contents of the ACFs, obtained hereby were 740-860 m2/g and 4-5.6%, respectively, at around 50 wt% of burn-off. FT-IR and XPS analyses identified the surface oxygen and nitrogen functional groups on the stabilized and activated fibers. The ACFs from isoquinoline pitch(IQP-ACF) exhibited higher basicity(1.3 meq/g) than commercial ACFs of similar surface areas(0.68 and 0.25 meq/g for PAN(FE-300) and coal tar pitch(OG-8A) based ACFs, respectively) due to a higher basic nitrogen content on the surface. The activation appears to expose basic nitrogen atoms, which were located under the surface. The basicity of ACF from quinoline pitch(QP-ACF) was much lower than that of IQP-ACF, however, QP-ACF adsorbed 74 mg/g of SO2. which was 1.4 and 2.3 times higher than that over FE-300 and OG-8A. In contrast, IQP-ACFs showed less adsorption of SO2 than that of QP-ACF and FE-300, but more than that of OG-8A. Oxidation activity of ACF surface may participate in the adsorpton of SO2 in the form of SO3 or H2SO4. The oxygen functional groups under the influence of neighboring nitrogen atoms may be the active sites for the oxidative adsorption.

本文言語英語
ページ(範囲)399-405
ページ数7
ジャーナルSekiyu Gakkaishi (Journal of the Japan Petroleum Institute)
41
6
DOI
出版ステータス出版済み - 1998

All Science Journal Classification (ASJC) codes

  • 燃料技術
  • エネルギー工学および電力技術

フィンガープリント

「Activated carbon fibers prepared from quinoline and isoquinoline pitches」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル