Adhesion enhancement of Poly(etheretherketone) via surface-initiated photopolymerization of glycidyl methacrylate

Yucheng Zhang, Koichi Hasegawa, Sota Kamo, Kiyoka Takagi, Atsushi Takahara

研究成果: Contribution to journalArticle査読

抄録

Poly(etheretherketone) (PEEK) is a high-performance engineering thermoplastic with high heat deflection temperature. Owing to its low surface free energy, the untreated PEEK adherend may exhibit low bond shear strength with epoxy adhesives. This work presents a method to improve the adhesion performance of PEEK with epoxy adhesives through poly(glycidyl methacrylate) (PGMA) grafting. The PGMA-grafted PEEK (PEEK-g-PGMA) was prepared via surface-initiated photopolymerization under 2 and 8 mW/cm2, respectively. The influence of the irradiation duration and the removal of the polymerization inhibitor from the monomer on PGMA grafting are discussed herein. The results showed that (1) the PEEK-g-PGMA is obtained from the photopolymerization under 2 and 8 mW/cm2 of UV irradiation; (2) the long durations of the UV exposure promoted the formation of brushes; and (3) the polymerization inhibitor only slightly inhibited the polymerization, but effectively prevented the auto-polymerization of monomer solution during the UV irradiation. The enhanced performance of the epoxy adhesives was demonstrated by the single-lap shear tests using PEEK-g-PGMA joints. Under optimized concoctions, the lap shear strength of PEEK-g-PGMA was significantly enhanced to 15.1 MPa which is seven times higher than that of unmodified PEEK (2.5 MPa).

本文言語英語
論文番号122971
ジャーナルpolymer
209
DOI
出版ステータス出版済み - 11 17 2020
外部発表はい

All Science Journal Classification (ASJC) codes

  • Organic Chemistry
  • Polymers and Plastics
  • Materials Chemistry

フィンガープリント 「Adhesion enhancement of Poly(etheretherketone) via surface-initiated photopolymerization of glycidyl methacrylate」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル