Age Hardening in Ultrafine-Grained Al-2 Pct Fe Alloy Processed by High-Pressure Torsion

Jorge M. Cubero-Sesin, Zenji Horita

    研究成果: Contribution to journalArticle査読

    13 被引用数 (Scopus)

    抄録

    A cast Al-2 wt pct Fe alloy was processed by high-pressure torsion (HPT) at room temperature and then subjected to artificial aging at temperatures of 373 K and 473 K (100 °C and 200 °C). The aging behavior was studied by Vickers microhardness measurements and by microstructural analyses using transmission electron microscopy and X-ray diffraction. The initial intermetallic structures, composed of a mixture of Al + Al6Fe and Al + Al3Fe eutectics phases, were partially dissolved in the matrix up to a supersaturation of ~1 wt pct Fe. The microstructure was refined by HPT to an ultrafine-grained level with a minimum grain size of ~120 nm in the matrix and a dispersion of particles less than 400 nm. Age hardening was achieved within 0.25 hours at 473 K (200 °C), to a maximum UTS of ~700 MPa as a result of nano-sized precipitation within the ultrafine grains. The uniform elongation exceeded ~12 pct even at intermediate levels of imposed strain by HPT, while it decreased to ~6 pct with the subsequent aging treatment. The thermal stability of the ultrafine-grained structure was verified to exceed 16 days at 373 K (100 °C) and 12 hours at 473 K (200 °C).

    本文言語英語
    ページ(範囲)2614-2624
    ページ数11
    ジャーナルMetallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
    46
    6
    DOI
    出版ステータス出版済み - 6 1 2015

    All Science Journal Classification (ASJC) codes

    • 凝縮系物理学
    • 材料力学
    • 金属および合金

    フィンガープリント

    「Age Hardening in Ultrafine-Grained Al-2 Pct Fe Alloy Processed by High-Pressure Torsion」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル