Aging and precipitation behavior in supersaturated Al-2%Fe alloy produced by high-pressure torsion

Jorge M. Cubero-Sesin, Masashi Watanabe, Makoto Arita, Zenji Horita

研究成果: 著書/レポートタイプへの貢献会議での発言

3 引用 (Scopus)

抄録

The aging behavior of a cast Al-2 wt.% Fe alloy processed by High-Pressure Torsion (HPT) at room temperature was studied by subsequent aging treatments at 200 °C. Observations by Transmission Electron Microscopy (TEM) revealed that the microstructure after HPT processing reached an ultrafine-grained level with an average grain size in the Al matrix of ~120 nm. The initial eutectic structures were fragmented into particles with sizes of less than 400 nm and partially dissolved in the matrix up to a supersaturated Fe content of ~1% as confirmed by X-Ray Diffraction (XRD) analysis. The peak-age condition was achieved within 0.25 h of aging, which provides the maximum hardness of ~200 HV. Analyses by high-resolution S/TEM show that round particles of Al6Fe with sizes of ~5-10 nm and semi-coherent with the matrix are the dominant precipitates in the peak-aged condition. The hardness increases by aging for 12 h above the as-HPT-processed level of 185 HV. The dominant precipitate phase transforms to Al3Fe in the over-aged condition with a loss of coherency during growth. Enhanced precipitation kinetics was observed because of high density of lattice defects induced by the HPT processing, which were also confirmed by significant recovery in the electrical conductivity of the samples after aging.

元の言語英語
ホスト出版物のタイトルAluminium Alloys, ICAA 2014
出版者Trans Tech Publications Ltd
ページ766-771
ページ数6
ISBN(印刷物)9783038351207
DOI
出版物ステータス出版済み - 1 1 2014
イベント14th International Conference on Aluminium Alloys, ICAA 2014 - Trondheim, ノルウェー
継続期間: 6 15 20146 19 2014

出版物シリーズ

名前Materials Science Forum
794-796
ISSN(印刷物)0255-5476

その他

その他14th International Conference on Aluminium Alloys, ICAA 2014
ノルウェー
Trondheim
期間6/15/146/19/14

Fingerprint

Torsional stress
torsion
Aging of materials
Precipitates
precipitates
hardness
matrices
Hardness
Transmission electron microscopy
transmission electron microscopy
Crystal defects
Processing
eutectics
Eutectics
X ray diffraction analysis
casts
grain size
recovery
Recovery
microstructure

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

これを引用

Cubero-Sesin, J. M., Watanabe, M., Arita, M., & Horita, Z. (2014). Aging and precipitation behavior in supersaturated Al-2%Fe alloy produced by high-pressure torsion. : Aluminium Alloys, ICAA 2014 (pp. 766-771). (Materials Science Forum; 巻数 794-796). Trans Tech Publications Ltd. https://doi.org/10.4028/www.scientific.net/MSF.794-796.766

Aging and precipitation behavior in supersaturated Al-2%Fe alloy produced by high-pressure torsion. / Cubero-Sesin, Jorge M.; Watanabe, Masashi; Arita, Makoto; Horita, Zenji.

Aluminium Alloys, ICAA 2014. Trans Tech Publications Ltd, 2014. p. 766-771 (Materials Science Forum; 巻 794-796).

研究成果: 著書/レポートタイプへの貢献会議での発言

Cubero-Sesin, JM, Watanabe, M, Arita, M & Horita, Z 2014, Aging and precipitation behavior in supersaturated Al-2%Fe alloy produced by high-pressure torsion. : Aluminium Alloys, ICAA 2014. Materials Science Forum, 巻. 794-796, Trans Tech Publications Ltd, pp. 766-771, 14th International Conference on Aluminium Alloys, ICAA 2014, Trondheim, ノルウェー, 6/15/14. https://doi.org/10.4028/www.scientific.net/MSF.794-796.766
Cubero-Sesin JM, Watanabe M, Arita M, Horita Z. Aging and precipitation behavior in supersaturated Al-2%Fe alloy produced by high-pressure torsion. : Aluminium Alloys, ICAA 2014. Trans Tech Publications Ltd. 2014. p. 766-771. (Materials Science Forum). https://doi.org/10.4028/www.scientific.net/MSF.794-796.766
Cubero-Sesin, Jorge M. ; Watanabe, Masashi ; Arita, Makoto ; Horita, Zenji. / Aging and precipitation behavior in supersaturated Al-2%Fe alloy produced by high-pressure torsion. Aluminium Alloys, ICAA 2014. Trans Tech Publications Ltd, 2014. pp. 766-771 (Materials Science Forum).
@inproceedings{e372886e86034e52a8b26402b0cf13ac,
title = "Aging and precipitation behavior in supersaturated Al-2{\%}Fe alloy produced by high-pressure torsion",
abstract = "The aging behavior of a cast Al-2 wt.{\%} Fe alloy processed by High-Pressure Torsion (HPT) at room temperature was studied by subsequent aging treatments at 200 °C. Observations by Transmission Electron Microscopy (TEM) revealed that the microstructure after HPT processing reached an ultrafine-grained level with an average grain size in the Al matrix of ~120 nm. The initial eutectic structures were fragmented into particles with sizes of less than 400 nm and partially dissolved in the matrix up to a supersaturated Fe content of ~1{\%} as confirmed by X-Ray Diffraction (XRD) analysis. The peak-age condition was achieved within 0.25 h of aging, which provides the maximum hardness of ~200 HV. Analyses by high-resolution S/TEM show that round particles of Al6Fe with sizes of ~5-10 nm and semi-coherent with the matrix are the dominant precipitates in the peak-aged condition. The hardness increases by aging for 12 h above the as-HPT-processed level of 185 HV. The dominant precipitate phase transforms to Al3Fe in the over-aged condition with a loss of coherency during growth. Enhanced precipitation kinetics was observed because of high density of lattice defects induced by the HPT processing, which were also confirmed by significant recovery in the electrical conductivity of the samples after aging.",
author = "Cubero-Sesin, {Jorge M.} and Masashi Watanabe and Makoto Arita and Zenji Horita",
year = "2014",
month = "1",
day = "1",
doi = "10.4028/www.scientific.net/MSF.794-796.766",
language = "English",
isbn = "9783038351207",
series = "Materials Science Forum",
publisher = "Trans Tech Publications Ltd",
pages = "766--771",
booktitle = "Aluminium Alloys, ICAA 2014",

}

TY - GEN

T1 - Aging and precipitation behavior in supersaturated Al-2%Fe alloy produced by high-pressure torsion

AU - Cubero-Sesin, Jorge M.

AU - Watanabe, Masashi

AU - Arita, Makoto

AU - Horita, Zenji

PY - 2014/1/1

Y1 - 2014/1/1

N2 - The aging behavior of a cast Al-2 wt.% Fe alloy processed by High-Pressure Torsion (HPT) at room temperature was studied by subsequent aging treatments at 200 °C. Observations by Transmission Electron Microscopy (TEM) revealed that the microstructure after HPT processing reached an ultrafine-grained level with an average grain size in the Al matrix of ~120 nm. The initial eutectic structures were fragmented into particles with sizes of less than 400 nm and partially dissolved in the matrix up to a supersaturated Fe content of ~1% as confirmed by X-Ray Diffraction (XRD) analysis. The peak-age condition was achieved within 0.25 h of aging, which provides the maximum hardness of ~200 HV. Analyses by high-resolution S/TEM show that round particles of Al6Fe with sizes of ~5-10 nm and semi-coherent with the matrix are the dominant precipitates in the peak-aged condition. The hardness increases by aging for 12 h above the as-HPT-processed level of 185 HV. The dominant precipitate phase transforms to Al3Fe in the over-aged condition with a loss of coherency during growth. Enhanced precipitation kinetics was observed because of high density of lattice defects induced by the HPT processing, which were also confirmed by significant recovery in the electrical conductivity of the samples after aging.

AB - The aging behavior of a cast Al-2 wt.% Fe alloy processed by High-Pressure Torsion (HPT) at room temperature was studied by subsequent aging treatments at 200 °C. Observations by Transmission Electron Microscopy (TEM) revealed that the microstructure after HPT processing reached an ultrafine-grained level with an average grain size in the Al matrix of ~120 nm. The initial eutectic structures were fragmented into particles with sizes of less than 400 nm and partially dissolved in the matrix up to a supersaturated Fe content of ~1% as confirmed by X-Ray Diffraction (XRD) analysis. The peak-age condition was achieved within 0.25 h of aging, which provides the maximum hardness of ~200 HV. Analyses by high-resolution S/TEM show that round particles of Al6Fe with sizes of ~5-10 nm and semi-coherent with the matrix are the dominant precipitates in the peak-aged condition. The hardness increases by aging for 12 h above the as-HPT-processed level of 185 HV. The dominant precipitate phase transforms to Al3Fe in the over-aged condition with a loss of coherency during growth. Enhanced precipitation kinetics was observed because of high density of lattice defects induced by the HPT processing, which were also confirmed by significant recovery in the electrical conductivity of the samples after aging.

UR - http://www.scopus.com/inward/record.url?scp=84904389941&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84904389941&partnerID=8YFLogxK

U2 - 10.4028/www.scientific.net/MSF.794-796.766

DO - 10.4028/www.scientific.net/MSF.794-796.766

M3 - Conference contribution

AN - SCOPUS:84904389941

SN - 9783038351207

T3 - Materials Science Forum

SP - 766

EP - 771

BT - Aluminium Alloys, ICAA 2014

PB - Trans Tech Publications Ltd

ER -