Aging behavior of ultrafine grained commercial A1-Mg-Si alloy severely deformed by ARB process

Daisuke Terada, Yoma Kaneda, Zenji Horita, Kenji Matsuda, Takumi Hamaoka, Shoichi Hirosawa, Nobuhiro Tsuji

    研究成果: Chapter in Book/Report/Conference proceedingConference contribution

    抄録

    A commercial A1-Mg-Si alloy (6061 aluminum alloy) was used in the present study. The material was solution treated and then severely deformed by accumulative roll-bonding (ARB) process up to 6 cycles corresponding to total equivalent strain of 4.8. Subsequently, the specimens ARB-processed by various cycles were aged at 100°C and 170°C. During aging at 170°C, the increment of hardness of the ARB-processed specimen decreased with increasing the number of the ARB cycles. The hardness of the specimen ARB processed by 6 cycles decreased after aging at 170°C, though the hardness of a conventional solution-treated specimen increased greatly. On the other hand, the hardness of the specimen ARB-processed by various cycles increased significantly after aging at 100°C, and the obtained hardness was quite larger than that of the conventional materials. After aging, the strength and elongation of the solution treated specimen increased and decreased, respectively. The result shows normal tradeoff relationship between strength and elongation. However, in the ARB-processed specimens, the strength as well as elongation increased after aging. Especially, the elongation increased greatly after aging at 100°C. The results suggest that good mechanical properties can be obtained by a combination of grain refinement by severe plastic deformation process and precipitation by aging at low temperature.

    本文言語英語
    ホスト出版物のタイトル8th Pacific Rim International Congress on Advanced Materials and Processing 2013, PRICM 8
    出版社John Wiley and Sons Inc.
    ページ3259-3264
    ページ数6
    ISBN(印刷版)9781632660008
    出版ステータス出版済み - 2013
    イベント8th Pacific Rim International Congress on Advanced Materials and Processing 2013, PRICM 8 - Waikoloa, HI, 米国
    継続期間: 8 4 20138 9 2013

    出版物シリーズ

    名前8th Pacific Rim International Congress on Advanced Materials and Processing 2013, PRICM 8
    4

    その他

    その他8th Pacific Rim International Congress on Advanced Materials and Processing 2013, PRICM 8
    国/地域米国
    CityWaikoloa, HI
    Period8/4/138/9/13

    All Science Journal Classification (ASJC) codes

    • 電子材料、光学材料、および磁性材料

    フィンガープリント

    「Aging behavior of ultrafine grained commercial A1-Mg-Si alloy severely deformed by ARB process」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル