alpha yields gamma TRANSFORMATION BEHAVIOR DURING HEATING FROM ( alpha plus gamma ) REGION IN 0. 18% CARBON STEEL.

Kaneaki Tsuzaki, Kenji Yamaguchi, Tadashi Maki, Imao Tamura

研究成果: Contribution to journalArticle査読

7 被引用数 (Scopus)

抄録

The transformation was delayed with increasing an initial amount of proeutectoid alpha before heating. When the amount of proeutectoid alpha before heating was the same, the transformation kinetics was delayed with increases in initial gamma grain size and the gamma yields alpha transformation temperature in the alpha plus gamma region. Microscopic observation showed that transformation proceeded only by the growth of pre-existing gamma , namely, the dissolution of proeutectoid alpha without nucleation of new gamma grains in the proeutectoid alpha particles before heating, the experimental data lay on a straight line and T//0//. //9 increased with increasing particle size.

本文言語英語
ページ(範囲)234-241
ページ数8
ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
74
7
出版ステータス出版済み - 7 1 1988
外部発表はい

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Physical and Theoretical Chemistry
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「alpha yields gamma TRANSFORMATION BEHAVIOR DURING HEATING FROM ( alpha plus gamma ) REGION IN 0. 18% CARBON STEEL.」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル