Amorphous V2O5/carbon composites as electrochemical supercapacitor electrodes

T. Kudo, Y. Ikeda, T. Watanabe, M. Hibino, M. Miyayama, H. Abe, K. Kajita

研究成果: ジャーナルへの寄稿記事

165 引用 (Scopus)

抜粋

High rate intercalation electrode performance of V2O5 gel/carbon composites has been demonstrated. A V2O5 sol was prepared by a reaction of metallic vanadium with a hydrogen peroxide solution. Acetylene black powder was added into the sol with acetone to yield a homogeneous suspension. A composite of amorphous V2O5 and carbon was loaded on a macroporous nickel current collector, and heat-treated at 120 °C to obtain a sample electrode. Electrochemical measurements were performed in some organic electrolytes like LiClO4/PC or LiPF6/γ-butyrolactone (γ-BL) at room temperature. It was confirmed that a composite electrode with the V2O5/carbon ratio of 0.7 in weight showed 54% of the ideal capacity, 360 mA h/g (4.2-2.0 V) based on V2O5, even at a very high rate discharge at 150 C or 54 A/g V2O5. The diffusion length of this host-guest system was estimated as 30-50 nm by means of a simulation of the discharge curves using a diffusion model assuming D̃=10-12 cm2/s. The reversibility was also satisfactory and no capacity loss was observed after thousands of times of discharge/charge cycles between 4.2 and 3.0 V at the rate of 20 C. A prototype electrode was fabricated by coating a thin layer of the composite on an Al sheet current collector using an applicator. It showed the capacity of 40 mA h/g electrode at a current density as high as 30 mA/cm2.

元の言語英語
ページ(範囲)833-841
ページ数9
ジャーナルSolid State Ionics
152-153
DOI
出版物ステータス出版済み - 12 1 2002
外部発表Yes

    フィンガープリント

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Materials Science(all)
  • Condensed Matter Physics

これを引用