An intermediate temperature solid oxide fuel cell using a La(Sr)Ga(Mg)O3 thin film prepared by pulsed laser deposition as electrolyte

Jingwang Yan, Makiko Enoki, Hiroshige Matsumoto, Tatsumi Ishihara

研究成果: Contribution to journalArticle査読

5 被引用数 (Scopus)

抄録

A dense La0.9Sr0.1Ga0.8Mg 0.2O3- δ (LSGM, 5 μm in thickness) /Ce 0.8Sm0.2O2- δ (SDC, 400 nm in thickness) bi-layer film was fabricated on a dense NiO (Fe3O4)-SDC anode substrate by a pulsed laser deposition method. After in-situ reduction, the substrate turned to be porous by the reduction of NiO and Fe 3O4 to Ni and Fe, and the porosity reached to 13.6 vol%. Stoichiometric composition of LSGM film was successfully prepared by optimizing the deposition parameters and the target composition. When Sm 0.6Sr0.4CoO3- δ (SSC) was used as cathode material, extremely high power density was achieved at relatively low temperature. The maximum power density reached to 3270, 1951, 612 and 80 mW/cm2 at 973, 873, 773 and 673 K, respectively. Detail analysis by current interruption method revealed that IR drop was still dominant internal resistance at low temperature and the overpotential of the anode and the cathode was not significant even at 673 K. Therefore, SOFC can be operated at temperature lower than 773 K by using LSGM thin film.

本文言語英語
ページ(範囲)945-950
ページ数6
ジャーナルElectrochemistry
73
11
DOI
出版ステータス出版済み - 11 2005

All Science Journal Classification (ASJC) codes

  • 電気化学

フィンガープリント

「An intermediate temperature solid oxide fuel cell using a La(Sr)Ga(Mg)O<sub>3</sub> thin film prepared by pulsed laser deposition as electrolyte」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル