### 抄録

We present a systematic theoretical investigation of the vibrational properties of C-doped single layer hexagonal boron nitride (h-BN). Our studies have been carried out by the forced vibrational method, which is based on the idea of mechanical resonance and efficient for very complex and large system. We have estimated the phonon density of states (PDOSs) of h-BCN network with random and regular distribution of C atoms. It is found that the PDOS greatly depends on the C distribution and coverage. For randomly distributed C atoms, we observe that the longitudinal and the transverse optical (LO) and (TO) phonon branches for in-plane motion are nondegenerate at the Γ-point of the Brillouin zone. We determine a critical value of C concentration for the onset of this C-induced vibrational transition. We have found that C concentrations of about 10% and higher, the E_{2} _{g} peak of h-BN has been reduced into a shoulder or it has completely disappeared. For h-BCN network with regular domains of C, the PDOSs changes more abruptly. With the increase of C concentration, the high frequency optical phonons peaks above the 1400 cm^{-1} increase linearly while the h-BN peaks below the 1400 cm^{-1} are broadened and distorted. The disorder causes the phonon modes to be localized in the real space. Phonon localization in the hybrid BCN network is studied and the extent of localization is quantified by the typical mode pattern and the localization length. Spatial analyses of the eigenvectors using typical mode patterns show that Γ-point of the LO and TO phonon modes is strongly localized and show random behavior within a region of several nanometers in the BCN structure. In particular at 1400 cm^{-1}, a typical localization length is on the order of ≈4 nm for randomly distributed C atoms and ≈8.5 nm for the regular domains of C of 20% concentration, while at 1590 cm^{-1}, these values are ≈2 nm and ≈4 nm for randomly distributed C atoms and regular domains of C, respectively. These results are expected to stimulate further studies aimed at better understanding of the phenomena allied with vibrational properties such as thermal conductivity, specific heat capacity, and electron-phonon interaction of h-BN and BCN networks.

元の言語 | 英語 |
---|---|

ページ（範囲） | 225-233 |

ページ数 | 9 |

ジャーナル | Computational Materials Science |

巻 | 94 |

発行部数 | C |

DOI | |

出版物ステータス | 出版済み - 11 1 2014 |

### Fingerprint

### All Science Journal Classification (ASJC) codes

- Computer Science(all)
- Chemistry(all)
- Materials Science(all)
- Mechanics of Materials
- Physics and Astronomy(all)
- Computational Mathematics

### これを引用

*Computational Materials Science*,

*94*(C), 225-233. https://doi.org/10.1016/j.commatsci.2014.04.047

**Analysis of vibrational properties of C-doped hexagonal boron nitride (h-BN).** / Islam, Md Sherajul; Ushida, Kenji; Satoru, Tanaka; Makino, Takayuki; Hashimoto, Akihiro.

研究成果: ジャーナルへの寄稿 › 記事

*Computational Materials Science*, 巻. 94, 番号 C, pp. 225-233. https://doi.org/10.1016/j.commatsci.2014.04.047

}

TY - JOUR

T1 - Analysis of vibrational properties of C-doped hexagonal boron nitride (h-BN)

AU - Islam, Md Sherajul

AU - Ushida, Kenji

AU - Satoru, Tanaka

AU - Makino, Takayuki

AU - Hashimoto, Akihiro

PY - 2014/11/1

Y1 - 2014/11/1

N2 - We present a systematic theoretical investigation of the vibrational properties of C-doped single layer hexagonal boron nitride (h-BN). Our studies have been carried out by the forced vibrational method, which is based on the idea of mechanical resonance and efficient for very complex and large system. We have estimated the phonon density of states (PDOSs) of h-BCN network with random and regular distribution of C atoms. It is found that the PDOS greatly depends on the C distribution and coverage. For randomly distributed C atoms, we observe that the longitudinal and the transverse optical (LO) and (TO) phonon branches for in-plane motion are nondegenerate at the Γ-point of the Brillouin zone. We determine a critical value of C concentration for the onset of this C-induced vibrational transition. We have found that C concentrations of about 10% and higher, the E2 g peak of h-BN has been reduced into a shoulder or it has completely disappeared. For h-BCN network with regular domains of C, the PDOSs changes more abruptly. With the increase of C concentration, the high frequency optical phonons peaks above the 1400 cm-1 increase linearly while the h-BN peaks below the 1400 cm-1 are broadened and distorted. The disorder causes the phonon modes to be localized in the real space. Phonon localization in the hybrid BCN network is studied and the extent of localization is quantified by the typical mode pattern and the localization length. Spatial analyses of the eigenvectors using typical mode patterns show that Γ-point of the LO and TO phonon modes is strongly localized and show random behavior within a region of several nanometers in the BCN structure. In particular at 1400 cm-1, a typical localization length is on the order of ≈4 nm for randomly distributed C atoms and ≈8.5 nm for the regular domains of C of 20% concentration, while at 1590 cm-1, these values are ≈2 nm and ≈4 nm for randomly distributed C atoms and regular domains of C, respectively. These results are expected to stimulate further studies aimed at better understanding of the phenomena allied with vibrational properties such as thermal conductivity, specific heat capacity, and electron-phonon interaction of h-BN and BCN networks.

AB - We present a systematic theoretical investigation of the vibrational properties of C-doped single layer hexagonal boron nitride (h-BN). Our studies have been carried out by the forced vibrational method, which is based on the idea of mechanical resonance and efficient for very complex and large system. We have estimated the phonon density of states (PDOSs) of h-BCN network with random and regular distribution of C atoms. It is found that the PDOS greatly depends on the C distribution and coverage. For randomly distributed C atoms, we observe that the longitudinal and the transverse optical (LO) and (TO) phonon branches for in-plane motion are nondegenerate at the Γ-point of the Brillouin zone. We determine a critical value of C concentration for the onset of this C-induced vibrational transition. We have found that C concentrations of about 10% and higher, the E2 g peak of h-BN has been reduced into a shoulder or it has completely disappeared. For h-BCN network with regular domains of C, the PDOSs changes more abruptly. With the increase of C concentration, the high frequency optical phonons peaks above the 1400 cm-1 increase linearly while the h-BN peaks below the 1400 cm-1 are broadened and distorted. The disorder causes the phonon modes to be localized in the real space. Phonon localization in the hybrid BCN network is studied and the extent of localization is quantified by the typical mode pattern and the localization length. Spatial analyses of the eigenvectors using typical mode patterns show that Γ-point of the LO and TO phonon modes is strongly localized and show random behavior within a region of several nanometers in the BCN structure. In particular at 1400 cm-1, a typical localization length is on the order of ≈4 nm for randomly distributed C atoms and ≈8.5 nm for the regular domains of C of 20% concentration, while at 1590 cm-1, these values are ≈2 nm and ≈4 nm for randomly distributed C atoms and regular domains of C, respectively. These results are expected to stimulate further studies aimed at better understanding of the phenomena allied with vibrational properties such as thermal conductivity, specific heat capacity, and electron-phonon interaction of h-BN and BCN networks.

UR - http://www.scopus.com/inward/record.url?scp=84926277661&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84926277661&partnerID=8YFLogxK

U2 - 10.1016/j.commatsci.2014.04.047

DO - 10.1016/j.commatsci.2014.04.047

M3 - Article

VL - 94

SP - 225

EP - 233

JO - Computational Materials Science

JF - Computational Materials Science

SN - 0927-0256

IS - C

ER -