Application of Diffraction-Amalgamated Grain Boundary Tracking to Fatigue crack propagation behavior in high strength aluminum alloy

Hui Li, Hiroyuki Toda, Kentaro Uesugi, Akihisa Takeuchi, Yoshio Suzuki, Masakazu Kobayashi

研究成果: ジャーナルへの寄稿記事

3 引用 (Scopus)

抜粋

Fatigue crack propagation behavior in a 7075-type Al alloy (Al-5.6%Zn-2.5%Mg-1.6%Cu) was investigated by applying Diffraction-Amalgamated Grain Boundary Tracking (DAGT), which provides grain morphologies and crystallographic orientations in three dimensions (3D). 3D crack morphologies at different propagation stages in the bulk of the sample were successfully obtained using synchrotron radiation X-ray microtomography (SRCT) technique. The apparent crack growth rate, da/dN, which varies significantly along a crack front line, was calculated. There are rapid acceleration and deceleration regions of da/dN due to the interaction with grain boundary (GB) and crack closure segments. Typical crack morphology under the influence of Mode II (in-plane shear) and Mode III (out-of-plane shear), such as crack deflection and twist, is detected by the observation of 2D tomographic slice image. A detailed direct assessment of microstructure-crack interaction behaviors has been achieved by applying the DAGT technique.

元の言語英語
ページ(範囲)424-428
ページ数5
ジャーナルMaterials Transactions
56
発行部数3
DOI
出版物ステータス出版済み - 1 1 2015

    フィンガープリント

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

これを引用