High pressure torsion (HPT) is a well-known procedure to impart severe plastic deformation (SPD) into metallic materials. It was reported that HPT produces grain sizes finer than those using other SPD processes such as equal-channel angular pressing (ECAP). However, the application of HPT has been restricted to thin disk samples. In this study, an HPT process was developed for use with bulk samples. This process is designated as Bulk-HPT for comparison with conventional Disk-HPT. Cylindrical samples of an Al-3%Mg-0.2%Sc alloy having dimensions of 10 mm in diameter and 8.6 mm in height were prepared for Bulk-HPT. The samples were strained under a pressure of 1 GPa for 2 turns at room temperature. Microstractural observations revealed that the samples contained regions having a grain size of ∼ 130 nm. Tensile testing showed a superplastic ductility ∼480 % at 673 K with an initial strain rate of 3.3×10-2 s-1.