Bearing damage evolution of a pinned joint in CFRP laminates under repeated tensile loading

Satoshi Seike, Yoshihiro Takao, Wen Xue Wang, Terutake Matsubara

研究成果: ジャーナルへの寄稿記事

11 引用 (Scopus)

抄録

A mechanical pinned joint in the CFRP laminates such as [0/±45/90]3S, [90/±45/0]3S, [0/±45/90]2S and [90/±45/0]2s is loaded statically and cyclically to finally obtain the critical condition for fatigue. It is derived that in the static loading, the critical damage that yields shear matrix crack is kink and the critical condition to the final failure is the appearance of kink in every inner 0° layer and that in the fatigue loading within the moderate load, the critical damage that yields shear matrix crack is almost always kink-like damage along the collapse front and at high load it is rather kink. Next, the non-elastic elongation of a joint at the maximum load subtracted by the one at 10th cycle is focused on and its capability is figured out for various stacking sequences. The critical value UNE, F* for the elongation rate change to the final fatigue failure is around 50-65 μm in the present material. The critical condition to the final fatigue failure and corresponding to UNE, F* is roughly the appearance of mostly kink-like damage in every inner 0° layer.

元の言語英語
ページ(範囲)72-81
ページ数10
ジャーナルInternational Journal of Fatigue
32
発行部数1
DOI
出版物ステータス出版済み - 1 1 2010

Fingerprint

Bearings (structural)
Laminates
Carbon fiber reinforced plastics
Kink
Damage
Fatigue
Fatigue of materials
Elongation
Cracks
Crack
Stacking
Critical value
carbon fiber reinforced plastic
Cycle

All Science Journal Classification (ASJC) codes

  • Modelling and Simulation
  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering
  • Industrial and Manufacturing Engineering

これを引用

Bearing damage evolution of a pinned joint in CFRP laminates under repeated tensile loading. / Seike, Satoshi; Takao, Yoshihiro; Wang, Wen Xue; Matsubara, Terutake.

:: International Journal of Fatigue, 巻 32, 番号 1, 01.01.2010, p. 72-81.

研究成果: ジャーナルへの寄稿記事

Seike, Satoshi ; Takao, Yoshihiro ; Wang, Wen Xue ; Matsubara, Terutake. / Bearing damage evolution of a pinned joint in CFRP laminates under repeated tensile loading. :: International Journal of Fatigue. 2010 ; 巻 32, 番号 1. pp. 72-81.
@article{7a9d6ff4af744c03a46580daebbdd5a8,
title = "Bearing damage evolution of a pinned joint in CFRP laminates under repeated tensile loading",
abstract = "A mechanical pinned joint in the CFRP laminates such as [0/±45/90]3S, [90/±45/0]3S, [0/±45/90]2S and [90/±45/0]2s is loaded statically and cyclically to finally obtain the critical condition for fatigue. It is derived that in the static loading, the critical damage that yields shear matrix crack is kink and the critical condition to the final failure is the appearance of kink in every inner 0° layer and that in the fatigue loading within the moderate load, the critical damage that yields shear matrix crack is almost always kink-like damage along the collapse front and at high load it is rather kink. Next, the non-elastic elongation of a joint at the maximum load subtracted by the one at 10th cycle is focused on and its capability is figured out for various stacking sequences. The critical value UNE, F* for the elongation rate change to the final fatigue failure is around 50-65 μm in the present material. The critical condition to the final fatigue failure and corresponding to UNE, F* is roughly the appearance of mostly kink-like damage in every inner 0° layer.",
author = "Satoshi Seike and Yoshihiro Takao and Wang, {Wen Xue} and Terutake Matsubara",
year = "2010",
month = "1",
day = "1",
doi = "10.1016/j.ijfatigue.2009.02.010",
language = "English",
volume = "32",
pages = "72--81",
journal = "International Journal of Fatigue",
issn = "0142-1123",
publisher = "Elsevier Limited",
number = "1",

}

TY - JOUR

T1 - Bearing damage evolution of a pinned joint in CFRP laminates under repeated tensile loading

AU - Seike, Satoshi

AU - Takao, Yoshihiro

AU - Wang, Wen Xue

AU - Matsubara, Terutake

PY - 2010/1/1

Y1 - 2010/1/1

N2 - A mechanical pinned joint in the CFRP laminates such as [0/±45/90]3S, [90/±45/0]3S, [0/±45/90]2S and [90/±45/0]2s is loaded statically and cyclically to finally obtain the critical condition for fatigue. It is derived that in the static loading, the critical damage that yields shear matrix crack is kink and the critical condition to the final failure is the appearance of kink in every inner 0° layer and that in the fatigue loading within the moderate load, the critical damage that yields shear matrix crack is almost always kink-like damage along the collapse front and at high load it is rather kink. Next, the non-elastic elongation of a joint at the maximum load subtracted by the one at 10th cycle is focused on and its capability is figured out for various stacking sequences. The critical value UNE, F* for the elongation rate change to the final fatigue failure is around 50-65 μm in the present material. The critical condition to the final fatigue failure and corresponding to UNE, F* is roughly the appearance of mostly kink-like damage in every inner 0° layer.

AB - A mechanical pinned joint in the CFRP laminates such as [0/±45/90]3S, [90/±45/0]3S, [0/±45/90]2S and [90/±45/0]2s is loaded statically and cyclically to finally obtain the critical condition for fatigue. It is derived that in the static loading, the critical damage that yields shear matrix crack is kink and the critical condition to the final failure is the appearance of kink in every inner 0° layer and that in the fatigue loading within the moderate load, the critical damage that yields shear matrix crack is almost always kink-like damage along the collapse front and at high load it is rather kink. Next, the non-elastic elongation of a joint at the maximum load subtracted by the one at 10th cycle is focused on and its capability is figured out for various stacking sequences. The critical value UNE, F* for the elongation rate change to the final fatigue failure is around 50-65 μm in the present material. The critical condition to the final fatigue failure and corresponding to UNE, F* is roughly the appearance of mostly kink-like damage in every inner 0° layer.

UR - http://www.scopus.com/inward/record.url?scp=70349983046&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=70349983046&partnerID=8YFLogxK

U2 - 10.1016/j.ijfatigue.2009.02.010

DO - 10.1016/j.ijfatigue.2009.02.010

M3 - Article

AN - SCOPUS:70349983046

VL - 32

SP - 72

EP - 81

JO - International Journal of Fatigue

JF - International Journal of Fatigue

SN - 0142-1123

IS - 1

ER -