Behavior of reduction and sintering in cementite powder

Makoto Egashira, Toshihiro Tsuchiyama, Setsuo Takaki

研究成果: Contribution to journalConference article

2 引用 (Scopus)

抜粋

In this study, the synthesis of cementite from iron oxide was firstly attempted. Then, reduction and sintering behavior of cementite powder was studied for developing a new way of steel making using cementite. It is confirmed that cementite can be obtained by the way to carbonize the iron oxide with H2-CH4 gas mixture. The cementite compact was completely reduced at 873 K-1273K. The porosity of samples became larger than the cementite compact at the reduction below 1023K, while that became smaller above 1073K. Although the porosity of the samples became the smallest at 1273K in all samples, the some big pores remained. The best temperature for reduction and sintering was around 1123K to obtain the optimum microstructure.

元の言語英語
ページ(範囲)4239-4244
ページ数6
ジャーナルMaterials Science Forum
426-432
発行部数5
DOI
出版物ステータス出版済み - 1 1 2003
イベントThermec 2003 Processing and Manufacturing of Advanced Materials - Madrid, スペイン
継続期間: 7 7 20037 11 2003

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント Behavior of reduction and sintering in cementite powder' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用