Bulky averaged microscopic information for ecap-processed cu using accelerator-based gamma-ray-induced positron annihilation spectroscopy and neutron diffraction

Toshihiro Ishibashi, Yo Tomota, Satoshi Sugaya, Hiroyuki Toyokawa, Tetsuya Hirade, Zenji Horita, Hiroshi Suzuki

    研究成果: Contribution to journalArticle査読

    2 被引用数 (Scopus)

    抄録

    Bulky averaged microstructural parameters such as vacancy density, texture and intergranular stress for 99.99% Cu subjected to equalchannel angular pressing (ECAP) were investigated using accelerator-based gamma-ray-induced positron annihilation spectroscopy (AIPAS) and neutron diffraction. The Doppler-broadening parameter S for the AIPAS positron annihilation peaks increased after the first ECAP cycle and then decreased slightly with additional ECAP cycles. When the samples were annealed, the S value for the sample subjected to eight ECAP cycles was found to decrease at a lower temperature than that for the sample subjected to one ECAP cycle. The texture and intergranular stresses generated by ECAP were determined by neutron diffraction analyses. Changes in full width at half maximum and intensity of the (111) and (200) neutron diffraction peaks monitored in situ during annealing indicated the early onset of recrystallization in the sample subjected to eight ECAP cycles. These bulky averaged data show good agreement with both local scanning electron microscopy/electron backscatter diffraction observations and the results of mechanical tests.

    本文言語英語
    ページ(範囲)1562-1569
    ページ数8
    ジャーナルMaterials Transactions
    54
    9
    DOI
    出版ステータス出版済み - 2013

    All Science Journal Classification (ASJC) codes

    • 材料科学(全般)
    • 凝縮系物理学
    • 材料力学
    • 機械工学

    フィンガープリント

    「Bulky averaged microscopic information for ecap-processed cu using accelerator-based gamma-ray-induced positron annihilation spectroscopy and neutron diffraction」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル