Calcite bone substitute prepared from calcium hydroxide compact using heat-treatment under carbon dioxide atmosphere

Kanji Tsuru, Akihiro Otsu, Michito Maruta, Alireza Valanezhad, Giichiro Kawachi, Akari Takeuchi, Shigeki Matsuya, Kunio Ishikawa

研究成果: Chapter in Book/Report/Conference proceedingConference contribution

3 被引用数 (Scopus)

抄録

The purpose of this study is to investigate whether calcite blocks with high mechanical property could be obtained for a short period from calcium hydroxide (Ca(OH)2) compact using heat-treatment under carbon dioxide (CO2) atmosphere. The Ca(OH)2 disks compacted with different pressure was heated at different temperature ranging from 200°C to 800°C for an hour under CO2 atmosphere. From the X-ray diffractometry, Ca(OH)2 converted into calcite along with the rise of the heating temperature. Small amount of unreacted Ca(OH)2 remained in samples heated at 600°C whereas samples treated at 800°C converted to calcite with very small amount of calcium oxide. The diametral tensile strength (DTS) value increased with the rise of heating temperature up to 600°C then decreased down to 800°C. Meanwhile, the porosity decreased with the rise of heating temperature up to 600°C then slightly increased up to 800°C. From the scanning electron microscope observation, grains grew bigger along with the rise of heating temperature. Intergranular space between grains decreased from 200°C to 600°C. The highest DTS value (14 MPa±1.3) at 600°C could be the result of lesser intergranular space due to sintering.

本文言語英語
ホスト出版物のタイトルBioceramics 23
ページ166-169
ページ数4
DOI
出版ステータス出版済み - 1 1 2012
イベント23rd Symposium and Annual Meeting of International Society for Ceramics in Medicine, ISCM 2011 - Istanbul, トルコ
継続期間: 11 6 201111 9 2011

出版物シリーズ

名前Key Engineering Materials
493-494
ISSN(印刷版)1013-9826

その他

その他23rd Symposium and Annual Meeting of International Society for Ceramics in Medicine, ISCM 2011
Countryトルコ
CityIstanbul
Period11/6/1111/9/11

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Calcite bone substitute prepared from calcium hydroxide compact using heat-treatment under carbon dioxide atmosphere」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル