Cathode Properties of Na3FePO4CO3 Prepared by the Mechanical Ball Milling Method for Na-ion Batteries

Baowei Xie, Ryo Sakamoto, Ayuko Kitajou, Kosuke Nakamoto, Liwei Zhao, Shigeto Okada, Yuki Fujita, Nobuto Oka, Tetsuaki Nishida, Wataru Kobayashi, Masaki Okada, Toshiya Takahara

研究成果: Contribution to journalArticle査読

4 被引用数 (Scopus)


The carbonophosphate Na3FePO4CO3 was synthesized by the mechanical ball milling method for the first time. The composition of the obtained sample with a higher amount of Fe2+ was Na2.66Fe2+ 0.66Fe3+ 0.34PO4CO3 as confirmed by Mössbauer analysis, owing to the good airtight properties of this method. The obtained samples in an organic electrolyte delivered an initial discharge capacity of 124 mAh/g at room temperature, and a larger discharge capacity of 159 mAh/g (1.66 Na+/mole) at 60 °C. With 17 m NaClO4 aqueous electrolyte, a discharge capacity of 161 mAh/g (1.69 Na+/mole) was delivered because of the high ionic conductivity of the concentrated aqueous electrolyte. During the charge-discharge process, the formation of Fe4+ after charging up to 4.5 V and the return of Fe2+ after discharging down to 1.5 V were detected by ex-situ X-ray absorption near edge structure (XANES) analysis.

ジャーナルScientific reports
出版ステータス出版済み - 12 1 2020

All Science Journal Classification (ASJC) codes

  • 一般


「Cathode Properties of Na<sub>3</sub>FePO<sub>4</sub>CO<sub>3</sub> Prepared by the Mechanical Ball Milling Method for Na-ion Batteries」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。