Cathodic performance of VOPO4 with various crystal phases for Li ion rechargeable battery

Bustam M. Azmi, Tatsumi Ishihara, Hiroyasu Nishiguchi, Yusaku Takita

研究成果: Contribution to journalArticle

49 引用 (Scopus)

抜粋

Cathodic performance of six different VOPO4 phases for Li ion rechargeable battery was investigated. It was found that VOPO4 exhibits a high flat discharge potential of 3.7 V for Li ion electrochemical intercalation and de-intercalation excepting for β- and -types. On the other hand, slightly higher flat discharge potential of 3.9 and 3.8 V was observed for β- and -types. Capacity for Li intercalation is strongly related with the crystal structure of VOPO4. In particular, δ-phase exhibits the largest reversible capacity of ca. 130 mAh/g among the examined VOPO4. High capacity for Li intercalation in δ-phase VOPO4 hardly decreased over 30 times of charge and discharge cycles. Although the reversible capacity decreased with increasing the current density for charge and discharge, large capacity of 80 mAh/g was still sustained at 0.4 mA/cm2 for δ-type VOPO4.

元の言語英語
ページ(範囲)165-170
ページ数6
ジャーナルElectrochimica Acta
48
発行部数2
DOI
出版物ステータス出版済み - 11 21 2002
外部発表Yes

All Science Journal Classification (ASJC) codes

  • Chemical Engineering(all)
  • Analytical Chemistry
  • Electrochemistry

フィンガープリント Cathodic performance of VOPO4 with various crystal phases for Li ion rechargeable battery' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用