Ce-doped LiF-SrF2 eutectic scintillators for thermal neutron detection produced at different solidification rates

Takayuki Yanagida, Yutaka Fujimoto, Kentaro Fukuda, Noriaki Kawaguchi, Kenichi Watanabe, Atsushi Yamazaki, Akira Uritani, Valery Chani

研究成果: Contribution to journalArticle査読

18 被引用数 (Scopus)

抄録

Ce 0.1% doped LiF-SrF2 eutectic scintillators were produced by vertical Bridgman method at various solidification rates of 1, 5, 20, 80, 320, and 1280 mm/hr. The LiF contained 95% of 6Li. The SEM images of the samples solidified at 1-80 mm/hr demonstrated clear lamellar structures. The α-ray induced radioluminescence spectra of the scintillators had intense emission peak at 310 and 330 nm due to the emission from Ce3+ 5d-4f transition of Ce:SrF2 layers. When the samples were irradiated with 252Cf neutrons, they exhibited almost the same light yields of 4500-5500 ph/n and typical decay times of 120-160 ns. The optimal layer thickness of LiF-SrF2 was determined to be 0.9 μm.

本文言語英語
ページ(範囲)1449-1454
ページ数6
ジャーナルOptical Materials
35
7
DOI
出版ステータス出版済み - 5 2013
外部発表はい

All Science Journal Classification (ASJC) codes

  • 電子材料、光学材料、および磁性材料
  • コンピュータ サイエンス(全般)
  • 原子分子物理学および光学
  • 分光学
  • 物理化学および理論化学
  • 有機化学
  • 無機化学
  • 電子工学および電気工学

フィンガープリント

「Ce-doped LiF-SrF<sub>2</sub> eutectic scintillators for thermal neutron detection produced at different solidification rates」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル