Characterization of the thermal conductivity of EB-PVD ZrO 2-Y 2O 3 coatings with a pulsed thermal imaging method

Byungkoog Jang, J. G. Sun, S. W. Kim, Y. S. Oh, H. T. Kim

研究成果: Contribution to journalArticle査読

6 被引用数 (Scopus)


ZrO 2-(2-8mol%)Y 2O 3 coatings were deposited on zirconia substrates by EB-PVD. The coated layer had a columnar microstructure with intercolumnar gaps between columnar grains. Nanosized pores could be observed around feather-like grains as well as inside the columnar grains. The main phase of all coated specimens was the tetragonal phase. However, the monoclinic and cubic phase of the second phase could be detected for ZrO 2-2mol%Y 2O 3 coatings and ZrO 2-(6-8mol%)Y 2O 3 coatings, respectively. The thermal conductivity of coatings was successfully evaluated with the pulsed thermal imaging method using a combined sample of coatings and a substrate. Both the thermal conductivity and heat capacity of Y 2O 3-doped ZrO 2 coatings tended to decrease with increasing amounts of Y 2O 3.

ジャーナルSurface and Coatings Technology
出版ステータス出版済み - 8 25 2012

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry

フィンガープリント 「Characterization of the thermal conductivity of EB-PVD ZrO <sub>2</sub>-Y <sub>2</sub>O <sub>3</sub> coatings with a pulsed thermal imaging method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。