Chloride-induced corrosion of steel bars in concrete with presence of gap at steel-concrete interface

Tarek Uddin Mohammed, Nobuaki Otsuki, Hidenori Hamada, Toru Yamaji

研究成果: ジャーナルへの寄稿記事

36 引用 (Scopus)

抄録

Corrosion of steel bars in concrete with the presence of gaps/voids at the steel-concrete interface is summarized herein based on the accelerated laboratory and several long-term exposure tests. For this, reinforced concrete specimens with a length of 12 cm, width of 23 cm, and height of 28 cm were made. Specially fabricated steel bars were embedded in the specimens to measure the macrocell and microcell corrosion. The specimens were exposed to an artificially created chloride-induced corrosion environment. Furthermore, corrosion of steel bars of 23-year, 10-year, and 16-month-old reinforced concrete specimens was also reported to verify the results obtained in the accelerated laboratory investigations. Generally, the presence of gaps/voids at the steel-concrete interface causes the complete loss of passivity with the presence of chloride. The regions with the gap become anodic locally. The degree of micro-cell corrosion is also higher at these regions. This phenomenon is very clear at the bottom half of the steel bars oriented perpendicular to the casting direction of concrete. It could not, however, be neglected for the steel bars oriented along the casting direction of concrete due to the poor compaction. From this study, the significance of making concrete without interfacial gaps/voids at the steel-concrete interface is clearly understood, which is necessary to ensure long-term durability of concrete structures.

元の言語英語
ページ(範囲)149-156
ページ数8
ジャーナルACI Materials Journal
99
発行部数2
出版物ステータス出版済み - 1 1 2002

Fingerprint

Steel
Chlorides
Concretes
Corrosion
Reinforced concrete
Casting
Concrete construction
Durability
Compaction

All Science Journal Classification (ASJC) codes

  • Civil and Structural Engineering
  • Building and Construction
  • Materials Science(all)

これを引用

Chloride-induced corrosion of steel bars in concrete with presence of gap at steel-concrete interface. / Mohammed, Tarek Uddin; Otsuki, Nobuaki; Hamada, Hidenori; Yamaji, Toru.

:: ACI Materials Journal, 巻 99, 番号 2, 01.01.2002, p. 149-156.

研究成果: ジャーナルへの寄稿記事

Mohammed, Tarek Uddin ; Otsuki, Nobuaki ; Hamada, Hidenori ; Yamaji, Toru. / Chloride-induced corrosion of steel bars in concrete with presence of gap at steel-concrete interface. :: ACI Materials Journal. 2002 ; 巻 99, 番号 2. pp. 149-156.
@article{9b8b6cbccfe04313bc82d5d6bd6399c9,
title = "Chloride-induced corrosion of steel bars in concrete with presence of gap at steel-concrete interface",
abstract = "Corrosion of steel bars in concrete with the presence of gaps/voids at the steel-concrete interface is summarized herein based on the accelerated laboratory and several long-term exposure tests. For this, reinforced concrete specimens with a length of 12 cm, width of 23 cm, and height of 28 cm were made. Specially fabricated steel bars were embedded in the specimens to measure the macrocell and microcell corrosion. The specimens were exposed to an artificially created chloride-induced corrosion environment. Furthermore, corrosion of steel bars of 23-year, 10-year, and 16-month-old reinforced concrete specimens was also reported to verify the results obtained in the accelerated laboratory investigations. Generally, the presence of gaps/voids at the steel-concrete interface causes the complete loss of passivity with the presence of chloride. The regions with the gap become anodic locally. The degree of micro-cell corrosion is also higher at these regions. This phenomenon is very clear at the bottom half of the steel bars oriented perpendicular to the casting direction of concrete. It could not, however, be neglected for the steel bars oriented along the casting direction of concrete due to the poor compaction. From this study, the significance of making concrete without interfacial gaps/voids at the steel-concrete interface is clearly understood, which is necessary to ensure long-term durability of concrete structures.",
author = "Mohammed, {Tarek Uddin} and Nobuaki Otsuki and Hidenori Hamada and Toru Yamaji",
year = "2002",
month = "1",
day = "1",
language = "English",
volume = "99",
pages = "149--156",
journal = "ACI Materials Journal",
issn = "0889-325X",
publisher = "American Concrete Institute",
number = "2",

}

TY - JOUR

T1 - Chloride-induced corrosion of steel bars in concrete with presence of gap at steel-concrete interface

AU - Mohammed, Tarek Uddin

AU - Otsuki, Nobuaki

AU - Hamada, Hidenori

AU - Yamaji, Toru

PY - 2002/1/1

Y1 - 2002/1/1

N2 - Corrosion of steel bars in concrete with the presence of gaps/voids at the steel-concrete interface is summarized herein based on the accelerated laboratory and several long-term exposure tests. For this, reinforced concrete specimens with a length of 12 cm, width of 23 cm, and height of 28 cm were made. Specially fabricated steel bars were embedded in the specimens to measure the macrocell and microcell corrosion. The specimens were exposed to an artificially created chloride-induced corrosion environment. Furthermore, corrosion of steel bars of 23-year, 10-year, and 16-month-old reinforced concrete specimens was also reported to verify the results obtained in the accelerated laboratory investigations. Generally, the presence of gaps/voids at the steel-concrete interface causes the complete loss of passivity with the presence of chloride. The regions with the gap become anodic locally. The degree of micro-cell corrosion is also higher at these regions. This phenomenon is very clear at the bottom half of the steel bars oriented perpendicular to the casting direction of concrete. It could not, however, be neglected for the steel bars oriented along the casting direction of concrete due to the poor compaction. From this study, the significance of making concrete without interfacial gaps/voids at the steel-concrete interface is clearly understood, which is necessary to ensure long-term durability of concrete structures.

AB - Corrosion of steel bars in concrete with the presence of gaps/voids at the steel-concrete interface is summarized herein based on the accelerated laboratory and several long-term exposure tests. For this, reinforced concrete specimens with a length of 12 cm, width of 23 cm, and height of 28 cm were made. Specially fabricated steel bars were embedded in the specimens to measure the macrocell and microcell corrosion. The specimens were exposed to an artificially created chloride-induced corrosion environment. Furthermore, corrosion of steel bars of 23-year, 10-year, and 16-month-old reinforced concrete specimens was also reported to verify the results obtained in the accelerated laboratory investigations. Generally, the presence of gaps/voids at the steel-concrete interface causes the complete loss of passivity with the presence of chloride. The regions with the gap become anodic locally. The degree of micro-cell corrosion is also higher at these regions. This phenomenon is very clear at the bottom half of the steel bars oriented perpendicular to the casting direction of concrete. It could not, however, be neglected for the steel bars oriented along the casting direction of concrete due to the poor compaction. From this study, the significance of making concrete without interfacial gaps/voids at the steel-concrete interface is clearly understood, which is necessary to ensure long-term durability of concrete structures.

UR - http://www.scopus.com/inward/record.url?scp=0036524516&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0036524516&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:0036524516

VL - 99

SP - 149

EP - 156

JO - ACI Materials Journal

JF - ACI Materials Journal

SN - 0889-325X

IS - 2

ER -