Competing crack initiation behaviors of a laser additively manufactured nickel-based superalloy in high and very high cycle fatigue regimes

Kun Yang, Qi Huang, Qingyuan Wang, Qiang Chen

研究成果: Contribution to journalArticle査読

12 被引用数 (Scopus)

抄録

Ultrasonic fatigue tests were performed to investigate high and very high cycle fatigue behaviors of a laser additively manufactured Inconel 718 (IN718) alloy in the as-deposited condition. The results indicate that the competition failure behavior between the surface and interior crack initiation results in the separate S-N curve. Both manufacturing defects (e.g., gas pore, lack of fusion) and columnar grains (matrix) observed in the microstructure could act as the original fatigue micro-cracks due to the effective restriction on manufacturing defects. The fatigue sensitivity levels increase successively in terms of the type, size, and location of the maximal micro-crack.

本文言語英語
論文番号105580
ジャーナルInternational Journal of Fatigue
136
DOI
出版ステータス出版済み - 7 2020

All Science Journal Classification (ASJC) codes

  • Modelling and Simulation
  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering
  • Industrial and Manufacturing Engineering

フィンガープリント 「Competing crack initiation behaviors of a laser additively manufactured nickel-based superalloy in high and very high cycle fatigue regimes」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル