Compositional and histological comparison of carbonate apatite fabricated by dissolution–precipitation reaction and Bio-Oss®

Kenji Fujisawa, Kazuya Akita, Naoyuki Fukuda, Kumiko Kamada, Takaharu Kudoh, Go Ohe, Takamitsu Mano, Kanji Tsuru, Kunio Ishikawa, Youji Miyamoto

研究成果: Contribution to journalArticle査読

10 被引用数 (Scopus)

抄録

Carbonate apatite (CO3Ap) is an inorganic component of bone. This study aimed to compare the composition and tissue response to of CO3Ap (CO3Ap-DP) fabricated by the dissolution–precipitation reaction using calcite as a precursor and Bio-Oss®, which is widely used in orthopedic and dental fields as a synthetic bone substitute. X-ray diffraction and Fourier transform infrared results showed that CO3Ap-DP and Bio-Oss® were both B-type carbonate apatite with low crystallinity. The average sizes of CO3Ap-DP and Bio-Oss® granules were 450 ± 58 and 667 ± 168μ m, respectively, and their carbonate contents were 12.1 ± 0.6 and 5.6 ± 0.1 wt%, respectively. CO3Ap-DP had a larger amount of CO3 than Bio-Oss® but higher crystallinity than Bio-Oss®. When a bone defect made at the femur of rabbits was reconstructed with CO3Ap-DP and Bio-Oss®, CO3Ap-DP granules were partially replaced with bone, whereas Bio-Oss® remained at 8 weeks after implantation. CO3Ap-DP granules elicited a significantly larger amount of new bone formation at the cortical bone portion than Bio-Oss® at 4 weeks after the implantation. The results obtained in the present study demonstrated that CO3Ap-DP and Bio-Oss® showed different behavior even though they were both classified as CO3Ap. The CO3 content in CO3Ap played a more important role than the crystallinity of CO3Ap for replacement to bone and high osteoconductivity. [Figure not available: see fulltext.].

本文言語英語
論文番号121
ジャーナルJournal of Materials Science: Materials in Medicine
29
8
DOI
出版ステータス出版済み - 8 1 2018

All Science Journal Classification (ASJC) codes

  • Biophysics
  • Bioengineering
  • Biomaterials
  • Biomedical Engineering

フィンガープリント 「Compositional and histological comparison of carbonate apatite fabricated by dissolution–precipitation reaction and Bio-Oss<sup>®</sup>」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル