Corrosion and fatigue behaviors of steel plates at the boundary with concrete

I. T. Kim, Shigenobu Kainuma, N. Hosomi

研究成果: 著書/レポートタイプへの貢献会議での発言

抄録

In order to investigate the corrosion and fatigue behaviors for structural steel members at the boundary with concrete, accelerated exposure tests and fatigue tests were carried out on model specimens consisting of a steel plate and a concrete block. The specimens were exposed in environment chamber, which is controlled by S6-cycle corrosion test conditions, during 150, 300, 450, and 600 days, respectively. After removing corrosion productions, the geometry of corroded surface of the steel plates was measured by a Laser Focus Measuring Systems, and fatigue tests of the corroded steel plates were performed. The measured geometric data represented time-dependent thickness loss and corrosion depth of the steel plates. Based on the results of fatigue test, relationship between testing period, corrosion depth and fatigue life was evaluated.

元の言語英語
ホスト出版物のタイトルProceedings of the 4th International Structural Engineering and Construction Conference, ISEC-4 - Innovations in Structural Engineering and Construction
ページ135-139
ページ数5
1
出版物ステータス出版済み - 2008
イベント4th International Structural Engineering and Construction Conference, ISEC-4 - Innovations in Structural Engineering and Construction - Melbourne, VIC, オーストラリア
継続期間: 9 26 20079 28 2007

その他

その他4th International Structural Engineering and Construction Conference, ISEC-4 - Innovations in Structural Engineering and Construction
オーストラリア
Melbourne, VIC
期間9/26/079/28/07

Fingerprint

Fatigue of materials
Concretes
Corrosion
Steel
Concrete blocks
Geometry
Lasers
Testing

All Science Journal Classification (ASJC) codes

  • Civil and Structural Engineering
  • Building and Construction

これを引用

Kim, I. T., Kainuma, S., & Hosomi, N. (2008). Corrosion and fatigue behaviors of steel plates at the boundary with concrete. : Proceedings of the 4th International Structural Engineering and Construction Conference, ISEC-4 - Innovations in Structural Engineering and Construction (巻 1, pp. 135-139)

Corrosion and fatigue behaviors of steel plates at the boundary with concrete. / Kim, I. T.; Kainuma, Shigenobu; Hosomi, N.

Proceedings of the 4th International Structural Engineering and Construction Conference, ISEC-4 - Innovations in Structural Engineering and Construction. 巻 1 2008. p. 135-139.

研究成果: 著書/レポートタイプへの貢献会議での発言

Kim, IT, Kainuma, S & Hosomi, N 2008, Corrosion and fatigue behaviors of steel plates at the boundary with concrete. : Proceedings of the 4th International Structural Engineering and Construction Conference, ISEC-4 - Innovations in Structural Engineering and Construction. 巻. 1, pp. 135-139, 4th International Structural Engineering and Construction Conference, ISEC-4 - Innovations in Structural Engineering and Construction, Melbourne, VIC, オーストラリア, 9/26/07.
Kim IT, Kainuma S, Hosomi N. Corrosion and fatigue behaviors of steel plates at the boundary with concrete. : Proceedings of the 4th International Structural Engineering and Construction Conference, ISEC-4 - Innovations in Structural Engineering and Construction. 巻 1. 2008. p. 135-139
Kim, I. T. ; Kainuma, Shigenobu ; Hosomi, N. / Corrosion and fatigue behaviors of steel plates at the boundary with concrete. Proceedings of the 4th International Structural Engineering and Construction Conference, ISEC-4 - Innovations in Structural Engineering and Construction. 巻 1 2008. pp. 135-139
@inproceedings{28c18cb186fe4169bdc4c2cd4deeefc1,
title = "Corrosion and fatigue behaviors of steel plates at the boundary with concrete",
abstract = "In order to investigate the corrosion and fatigue behaviors for structural steel members at the boundary with concrete, accelerated exposure tests and fatigue tests were carried out on model specimens consisting of a steel plate and a concrete block. The specimens were exposed in environment chamber, which is controlled by S6-cycle corrosion test conditions, during 150, 300, 450, and 600 days, respectively. After removing corrosion productions, the geometry of corroded surface of the steel plates was measured by a Laser Focus Measuring Systems, and fatigue tests of the corroded steel plates were performed. The measured geometric data represented time-dependent thickness loss and corrosion depth of the steel plates. Based on the results of fatigue test, relationship between testing period, corrosion depth and fatigue life was evaluated.",
author = "Kim, {I. T.} and Shigenobu Kainuma and N. Hosomi",
year = "2008",
language = "English",
isbn = "0415457556",
volume = "1",
pages = "135--139",
booktitle = "Proceedings of the 4th International Structural Engineering and Construction Conference, ISEC-4 - Innovations in Structural Engineering and Construction",

}

TY - GEN

T1 - Corrosion and fatigue behaviors of steel plates at the boundary with concrete

AU - Kim, I. T.

AU - Kainuma, Shigenobu

AU - Hosomi, N.

PY - 2008

Y1 - 2008

N2 - In order to investigate the corrosion and fatigue behaviors for structural steel members at the boundary with concrete, accelerated exposure tests and fatigue tests were carried out on model specimens consisting of a steel plate and a concrete block. The specimens were exposed in environment chamber, which is controlled by S6-cycle corrosion test conditions, during 150, 300, 450, and 600 days, respectively. After removing corrosion productions, the geometry of corroded surface of the steel plates was measured by a Laser Focus Measuring Systems, and fatigue tests of the corroded steel plates were performed. The measured geometric data represented time-dependent thickness loss and corrosion depth of the steel plates. Based on the results of fatigue test, relationship between testing period, corrosion depth and fatigue life was evaluated.

AB - In order to investigate the corrosion and fatigue behaviors for structural steel members at the boundary with concrete, accelerated exposure tests and fatigue tests were carried out on model specimens consisting of a steel plate and a concrete block. The specimens were exposed in environment chamber, which is controlled by S6-cycle corrosion test conditions, during 150, 300, 450, and 600 days, respectively. After removing corrosion productions, the geometry of corroded surface of the steel plates was measured by a Laser Focus Measuring Systems, and fatigue tests of the corroded steel plates were performed. The measured geometric data represented time-dependent thickness loss and corrosion depth of the steel plates. Based on the results of fatigue test, relationship between testing period, corrosion depth and fatigue life was evaluated.

UR - http://www.scopus.com/inward/record.url?scp=55549093792&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=55549093792&partnerID=8YFLogxK

M3 - Conference contribution

SN - 0415457556

SN - 9780415457552

VL - 1

SP - 135

EP - 139

BT - Proceedings of the 4th International Structural Engineering and Construction Conference, ISEC-4 - Innovations in Structural Engineering and Construction

ER -