Corrosion behavior of Al-7wt% Sl-1.5wt% Cu severely deformed by equal-channel angular pressing

Zuogui Zhang, Eiji Akiyama, Yoshimi Watanabe, Yasuyuki Katada, Kaneaki Tsuzaki

研究成果: Chapter in Book/Report/Conference proceedingConference contribution

2 被引用数 (Scopus)

抄録

In this study, an Al-7 wt% Si-1.5 wt% Cu alloy was subjected to severe plastic deformation (SPD) by an equal-channel angular pressing (ECAP) technique. The ECAP process was repetitively carried out up to 8 passes using a strain introduction method of route Bc, at a temperature of 25 °C and a pressing rate of 0.33 mm s-1. Microstructures of the samples before and after ECAP were observed by a scanning electron microscopy (SEM). Electrochemical properties of the Al-Si-Cu alloy fabricated by ECAP have been investigated in a borate-boric acid buffer solution containing Cl- ions at pH 8.3 and 25 °C by potentiodynamic polarization test. Corrosion pits on the sample surface after anodic polarization were investigated by means of SEM. The anodic polarization showed that as-cast Al-Si-Cu alloy with plate-shaped Si particles has poor resistance against pitting corrosion comparing to quenched sample without ECAP. Pitting potentials of ECAPed Al-Si-Cu alloy samples were higher than that of the sample without ECAP. In the Al-Si-Cu alloy, the corrosion pits were found in the region of Si particles and the size of pits formed on the ECAPed samples became smaller than that without ECAP. It is considered that the improvement of the pitting resistance of ECAPed Al-Si-Cu alloy is due to homogenous distribution of spherical Si particles generated during ECAP process.

本文言語英語
ホスト出版物のタイトルSupplement to THERMEC 2006, 5th International Conference on PROCESSING and MANUFACTURING OF ADVANCED MATERIALS, THERMEC 2006
ページ2892-2897
ページ数6
PART 3
出版ステータス出版済み - 12 1 2007
外部発表はい
イベント5th International Conference on Processing and Manufacturing of Advanced Materials - THERMEC'2006 - Vancouver, カナダ
継続期間: 7 4 20067 8 2006

出版物シリーズ

名前Materials Science Forum
番号PART 3
539-543
ISSN(印刷版)0255-5476

その他

その他5th International Conference on Processing and Manufacturing of Advanced Materials - THERMEC'2006
国/地域カナダ
CityVancouver
Period7/4/067/8/06

All Science Journal Classification (ASJC) codes

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Corrosion behavior of Al-7wt% Sl-1.5wt% Cu severely deformed by equal-channel angular pressing」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル