Crystal orientation and microstructure of CeO2 thin films grown on biaxially textured metallic substrates

Kaname Matsumoto, Hideyuki Shii, Ataru Ichinose, Hiroki Adachi, Yutaka Yoshida, Shigeru Horii, Masashi Mukaida, Kozo Osamura

研究成果: Contribution to journalArticle査読

2 被引用数 (Scopus)

抄録

We have fabricated biaxially textured Ni and Ni-0.1 mass%Cr (Ni-Cr) tapes, and crystal orientation and microstructure of CeO2 films deposited on the tapes by pulsed laser deposition were investigated. Recrystallized Ni-Cr tapes had a strong cube texture, {100} 〈001〈 orientation, and the surface of the tapes was occupied by the (100) oriented grains. CeO2 films grown on the Ni-Cr surface showed both the (100) preferred orientation and the strong in-plane alignment. Although recrystallized Ni tapes exhibited the {100}〈001〈 texture and the CeO2 films subsequently deposited on the tapes also have (100) orientation, a large number of (111) oriented grains were included in the films. The difference between the films deposited on the Ni-Cr and the pure Ni tapes depended on the degree of the cube texture and the surface flatness of the tapes. The preferred orientation of CeO2 films was also affected by the oxygen partial pressure during pulsed laser deposition, and the strong (100) orientation was attained under the pressure of 2.7 × 10-3 Pa. Moreover, the degree of the (100) orientation of CeO2 films was improved with increase of the film thickness. The microstructure of the films and its texture evolution mechanism were discussed.

本文言語英語
ページ(範囲)730-736
ページ数7
ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
68
9
DOI
出版ステータス出版済み - 1 1 2004
外部発表はい

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Crystal orientation and microstructure of CeO<sub>2</sub> thin films grown on biaxially textured metallic substrates」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル