Crystallographic orientation dependence of ε martensite transformation during tensile deformation of polycrystalline 30% Mn austenitic steel

Rintaro Ueji, Yoshinori Takagi, Noriyuki Tsuchida, Kazunari Shinagawa, Yasuhiro Tanaka, Takashi Mizuguchi

研究成果: Contribution to journalArticle査読

29 被引用数 (Scopus)

抄録

The dependence of the ε martensite transformation on the crystallographic orientation during a tensile test of metastable high-manganese austenitic steel, Fe–30 mass% Mn, with a polycrystalline microstructure was studied. The ε martensite plates were formed after the steel yielded by slipping, and the volume fraction of the ε martensite increased with increasing strain. No significant orientation dependence of the martensite formation was observed in the early stage of the tensile deformation, but when the sample was further strained up to about 30%, the tensile directions of the grains with martensite were preferentially found to be nearly parallel to the 〈111〉 direction of the austenite matrix. This orientation dependence corresponded with the orientation preferable for the development of local misorientations as detected by EBSD.

本文言語英語
ページ(範囲)14-20
ページ数7
ジャーナルMaterials Science and Engineering A
576
DOI
出版ステータス出版済み - 8 1 2013
外部発表はい

All Science Journal Classification (ASJC) codes

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Crystallographic orientation dependence of ε martensite transformation during tensile deformation of polycrystalline 30% Mn austenitic steel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル