Crystallographic orientation-dependent growth mode of microstructurally fatigue small crack in a laminated Ti-6Al-4V alloy

Akira Maenosono, Motomichi Koyama, Yoshihisa Tanaka, Shien Ri, Qinghu Wang, Hiroshi Noguchi

研究成果: Contribution to journalConference article

1 引用 (Scopus)

抜粋

The fatigue life of Ti-6Al-4V alloy exhibits significant scatter, which is derived from the statistical scatter of uncontrollable material factors. In particular, crack propagation behaviors in microstructurally small cracks strongly depend on material factors. It is necessary to understand the mechanisms underlying the scatter of fatigue properties. In this study, the dominant material/mechanical factors of microstructurally small fatigue crack growth behaviors are extracted, and the mechanisms of fatigue crack propagation life scatter derived from them are clarified. A Ti-6Al-4V billet was studied in which the microstructure was fully laminated with α and β phases. The major constituent phase was α. Microstructurally small artificial defects were introduced at a center of prior β grains by a focused ion beam (FIB). A fatigue test was carried out at a stress ratio R = 0, stress amplitude σa = 400 MPa, and frequency 1.3 × 10 -2 Hz in a vacuum using scanning electron microscopy (SEM). In situ SEM observation was carried out around each FIB notch. After the fatigue test, the dependence of the crack growth path on crystallographic orientation was investigated by using electron backscattered diffraction. It was found that microstructurally small crack growth behaviors depended on crystallographic orientation. The dominant crack growth mechanism was the mode II crack growth mechanism by shear stress along the basal plane as a driving force. The dominant factor that causes large scatter of fatigue life in a α- Ti-6Al-4V alloy is the difference in resolved shear stress along the basal plane. Specifically, the difference in the angle between the basal plane and loading direction, the low reproducibility of the mode II crack growth mechanism, and the random position of pre-existing damage cause the scatter of fatigue crack growth rate.

元の言語英語
ページ(範囲)694-699
ページ数6
ジャーナルProcedia Structural Integrity
13
DOI
出版物ステータス出版済み - 1 1 2018
イベント22nd European Conference on Fracture, ECF 2018 - Belgrade, セルビア
継続期間: 8 25 20188 26 2018

All Science Journal Classification (ASJC) codes

  • Mechanical Engineering
  • Mechanics of Materials
  • Civil and Structural Engineering
  • Materials Science(all)

フィンガープリント Crystallographic orientation-dependent growth mode of microstructurally fatigue small crack in a laminated Ti-6Al-4V alloy' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用