円孔を有する縫合CFRP積層板の損傷進展

吉村 彰記, 矢代 茂樹, 武田 展雄

研究成果: Contribution to journalArticle査読

抄録

This study experimentally and numerically investigated the tensile damage progress in stitched CFRP laminate with an open-hole. Detailed damage observation in the tensile tests revealed that stitching had almost no effect on the onset of the ply cracks. Delamination also appeared at the all ply interfaces near the hole, and was connected by neighboring ply cracks. We then performed damage extension simulation for holed stitched-laminate using a layer-wise finite element model with cohesive elements for the damage (ply cracks and delamination) and beam elements as stitch threads. Simulation results confirmed that the delamination extended toward the area surrounded by the ply cracks in the neighboring two layers and the edge of the open-hole. Moreover, we demonstrated that stitching could suppress the delamination progress from the hole edge.
寄稿の翻訳タイトルDamage Progress in the Stitched CFRP Laminates with Open-Hole
本文言語Japanese
ページ(範囲)14-20
ページ数7
ジャーナル日本複合材料学会誌
34
1
DOI
出版ステータス出版済み - 1 15 2008

フィンガープリント 「円孔を有する縫合CFRP積層板の損傷進展」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル