Fine decagonal phase lamellae-bearing icosahedral Al-Pd-Mn quasicrystals were tested compressionally at temperatures of 997 to 1073 K and initial strain rate of 3 × 10-5 to 1 × 10-4 s-1, and stress relaxation tests were performed at various stages of deformation. The results confirmed the thermally activated nature of deformation, and the stress exponent of strain rate was around 4. Internal stress for deformation estimated by Kikuchi's method reached 50 to 90% of applied stress. The effective stress exponent of strain rate was revealed to be about 1.3. At least a part of high internal stress was attributable to complicated dislocation microstructure.