Dense/porous asymmetric-structured oxygen permeable Membranes based on la0.6Ca0.4CoO3 perovskite-type oxide

Ken Watanabe, Masayoshi Yuasa, Tetsuya Kida, Kengo Shimanoe, Yasutake Teraoka, Noboru Yamazoe

研究成果: ジャーナルへの寄稿記事

32 引用 (Scopus)

抜粋

To achieve high-efficiency oxygen permeation using mixed (ionic and electronic) conducting perovskite-type oxides, we examined asymmetric-structured membranes of La0.6Ca0.4CoO3 in which a thin dense membrane was deposited on a porous support. The La0.6Ca 0.4CoO3 porous support was fabricated using irregular-shaped precursor particles prepared through an oxalate method. The fabricated support had good gas permeability and thermal stability, showing sufficient properties as a support for dense thin membranes. A dense membrane of 10 μm thickness was successfully formed on the porous support by coating a La0.6Ca0.4CoO3 slurry and subsequent densification by sintering. The deposited thin membrane was gastight and free from clacks, as revealed by gas permeation tests and SEM observations. The asymmetric membrane exhibited a high oxygen permeability of 1.66 cm3 (STP, standard temperature and pressure) min-1 cm-2 at 930 °C, which was four times higher than that of a typical sintered-disk type membrane with 1200 μm thickness, demonstrating its feasibility as a high-performance oxygen separation membrane.

元の言語英語
ページ(範囲)6965-6973
ページ数9
ジャーナルChemistry of Materials
20
発行部数22
DOI
出版物ステータス出版済み - 11 25 2008

    フィンガープリント

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Chemical Engineering(all)
  • Materials Chemistry

これを引用